Abstract:Electrochemical binders used to immobilize electrocatalysts on electrodes are essential in all fields of electrochemistry. Yet conventional organic-based binders like Nafion generally suffer from oxidative decomposition at high potential on anodic electrodes, as well as from a high charge transport resistivity. This work proposes the acidic redox-assisted deposition of cobalt manganese oxyhydroxides (CMOH) as a solid-state inorganic binder. CMOH is stable at high oxidative current and ensures catalyst adhesion even under strong peel-off stress as shown by experiments conducting alkaline oxygen evolution reaction (OER) using a RuO2 as catalyst immobilized on a rotating disc electrode. While the molecular structure of Nafion decays significantly after 45 minutes under OER conditions at 3.86 V, CMOH binder is able to support the powder catalysts (RuO2 and NiOx) performing stability around 1000 mA•cm-2 without significant current decay for 24 hours. The robust catalyst adhesion is a result of the formation of chemical bonds between the electrode and the binder and can be further improved by increasing the applied loading of CMOH. Different to Nafion, both the OER activity and the diffusion kinetics are not significantly affected by the CMOH binder. It has further been shown that using CMOH as binder leads to lower charge transfer resistances Rct and higher electrochemical surface areas compared to systems using Nafion. This is partially related to the presence of metal sites in different oxidation states which has been discussed to cause an increased intrinsic conductivity facilitating the charge hopping at the binder/electrocatalyst interface. With that, the present work provides proof-of-concept of inorganic metal oxide as a promising solid-state binder for a wider range of applications in electrochemistry, demonstrating CMOH's outstanding characteristic of strong adhesion to support other highly active but adhesion-weak electrocatalysts.

In-situ removal of surface molybdenum oxide making binder-free porous Mo1.98C1.02 film as a more efficient electrocatalyst for alkaline than for acidic hydrogen production

Thein Situremoval of Surface Molybdenum Oxide for Making Binder-Free Porous Mo1.98C1.02film a More Efficient Electrocatalyst for Alkaline Rather Than Acidic Hydrogen Production

Highly Efficient Electrocatalytic Hydrogen Evolution Promoted by O–Mo–C Interfaces of Ultrafine Β-Mo2c Nanostructures†

Self-supporting composited electrocatalysts of ultrafine Mo<sub>2</sub>C on 3D-hierarchical porous carbon monoliths for efficient hydrogen evolution

Porous Molybdenum Carbide Nanostructures Synthesized on Carbon Cloth by CVD for Efficient Hydrogen Production

Bimetallic MOF-Templated Fabrication of Porous Zn, N Co-doped Mo 2 C for an Efficient Hydrogen Evolution Reaction

Well-Defined Mo2C Nanoparticles Embedded in Porous N-Doped Carbon Matrix for Highly Efficient Electrocatalytic Hydrogen Evolution

Surface Ammonium Ions Assisted Decoration of Monodisperse Cobalt Nanoparticles on Molybdenum Oxide Films as Efficient Electrocatalysts for Hydrogen Evolution Reaction

General synthesis of nanostructured Mo2C electrocatalysts using a carbon template for electrocatalytic applications

Highly active and durable nanostructured molybdenum carbide electrocatalysts for hydrogen production

Organic-Inorganic-Hybrid-Derived Molybdenum Carbide Nanoladders: Impacts of Surface Oxidation for Hydrogen Evolution Reaction

Defined organic-octamolybdate crystalline superstructures derived Mo 2 C@C as efficient hydrogen evolution electrocatalysts

All‐pH Stable Sandwich‐Structured MoO 2 /MoS 2 /C Hollow Nanoreactors for Enhanced Electrochemical Hydrogen Evolution

A 2D free-standing film-inspired electrocatalyst for highly efficient hydrogen production

Mesoporous and Skeletal Molybdenum Carbide for Hydrogen Evolution Reaction: Diatomite‐type Structure and Formation Mechanism

Controllable synthesis of molybdenum-based electrocatalysts for a hydrogen evolution reaction

One-step molten-salt synthesis of adjustable composition molybdenum carbide-based electrocatalysts for hydrogen evolution in both acidic and alkaline media

Robust Inorganic Binder Against Corrosion and Peel-Off Stress in Electrocatalysis

Mo2C nanospheres anchored on nickel foam as self-supported electrode for high-performance hydrogen production

Enhanced electrocatalytic hydrogen evolution by molybdenum disulfide nanodots anchored on MXene under alkaline conditions

Unraveling the oxide layer on Mo2C as the active center for hydrogen evolution reaction