The microwave-absorption properties and mechanism of phenyl silicone rubber/CIPs/graphene composites after thermal-aging in an elevated temperature

Xiao Yan,Jianhua Guo,Xinghua Jiang

DOI: https://doi.org/10.1038/s41598-022-08415-6

IF: 4.6

2022-03-14

Scientific Reports

Abstract:Abstract Recently, the application and development of flexible microwave-absorption composites based on silicone rubber have gradually become a research hot spot. In this study, methyl vinyl phenyl silicone rubber (MPVQ)/carbonyl iron particles (CIPs)/graphene (GR) composites were prepared by mechanical blending, and the effects of thermal-ageing temperature on the microwave-absorption properties of the composites were investigated. The mechanism of the thermal-ageing temperature’s effects on microwave-absorption behaviour was identified. The results show that unaged composites have superior microwave-absorption properties, with a minimum reflection loss ( RL min ) of − 87.73 dB, a lowest thickness of 1.46 mm, and an effective absorption bandwidth ( EAB , RL < − 10 dB) reaching 5.8 GHz (9.9–15.7 GHz). With ageing at 240 °C for 24 h, the RL min at a frequency of 5.48 GHz is − 45.55 dB with a thickness of 2.55 mm, and the EAB value reaches 2 GHz (range 4.6–6.6 GHz). In the thermal-ageing process, a crosslinking reaction occurs in MPVQ with an increase in crosslinking density from 5.88 × 10 −5 mol g −1 (unaged) to 4.69 × 10 −4 mol g −1 (aged at 240 °C). Simultaneously, thermal degradation of the composites leads to a reduction in the rubber concentration. In addition, a small amount of CIPs are oxidized to Fe 3 O 4 , and the remaining CIPs aggregate to generate more electrically conductive pathways. Consequently, the dielectric loss of the composites will be significantly improved, resulting in poor impedance matching. The microwave-absorption properties of the composites gradually decrease with increasing thermal-ageing temperature from 200 to 240 °C.

multidisciplinary sciences