Unveiling and Overcoming Instabilities in Perovskite Solar Cells Induced by Atomic‐Layer‐Deposition Tin Oxide

Zhuo Zheng,Zexu Xue,Kai Zhao,Yuanhang Yang,Xueliang Zhu,Hao Li,Siyang Cheng,Sheng Li,Ning Yan,Zhiping Wang
DOI: https://doi.org/10.1002/solr.202301076
IF: 9.1726
2024-03-24
Solar RRL
Abstract:Atomic layer deposition of tin oxide (ALD‐SnO x ) has emerged as a promising buffer/protection layer, often replacing bathocuproine (BCP) in applications such as semitransparent and tandem devices. However, the long‐term stability and underlying degradation mechanisms of perovskite solar cells incorporating ALD‐SnO x remain elusive. Here we systematically investigate the long‐term stability of perovskite solar cells featuring an ALD‐SnO x buffer layer. Intriguingly, we observe that cells with ALD‐SnO x exhibit heightened susceptibility to severe degradation, surpassing even the degradation levels observed with BCP under humid conditions. Through an extensive analysis employing X‐ray photoelectron spectroscopy (XPS) and X‐ray diffraction (XRD), we unveil that ALD‐SnO x triggers a phase transition in the perovskite when exposed to moisture, transitioning from the black cubic phase to the yellow delta phase, despite the presence of a thin layer of fullerene between the SnO x and the perovskite. Replacing ALD‐SnO x with ALD‐AlO x as a buffer layer emerges as a transformative strategy, effectively bolstering the humidity and thermal stability of the cells, without affecting device efficiency. The optimized ALD‐AlO x ‐buffered device exhibits a high efficiency of 24.61% and maintains 88% of its initial efficiency after maximum power point tracking under one sun illumination for 1350 hours at 65°C in ambient air when encapsulated. This article is protected by copyright. All rights reserved.
energy & fuels,materials science, multidisciplinary
What problem does this paper attempt to address?