Nd3+ doped CaLaGa3O7: Growth, structure, and optical properties of a disordered laser crystal

Yunyun Liu,Fei Pan,Ju Gao,Chaoyang Tu

DOI: https://doi.org/10.1016/j.jlumin.2022.118748

IF: 3.6

2022-04-01

Journal of Luminescence

Abstract:A new disordered crystal of Nd3+-doped CaLaGa3O7 (Nd: CLGO) was successfully grown using the Czochralski method for the first time. The effective segregation coefficient of Nd3+ ions in CLGO was calculated to be 0.68. A systematic investigation of the crystal structure characteristics, fluorescence lifetime, polarized absorption spectra, and emission spectra of Nd: CLGO crystal at room temperature was reported. The maximal absorption cross-sections at 808 nm were 3.18 and 1.34 × 10−20 cm2 for π-polarization and σ-polarization with an FWHM of 16 and 10 nm, respectively, indicating the good pumping efficiency of laser diodes (LDs). The emission cross-sections at 1061 nm of π- and σ-polarization were 7.23 and 6.90 × 10−20 cm2 with an FWHM of 18.8 and 27.8 nm, respectively. Moreover, the measured fluorescence lifetime was 250 μs? Based on the spectral parameters, several important laser parameters were calculated to assess the laser capability. The above results indicate that Nd: CLGO crystal is a promising disordered laser host with AlGaAs LD pumping, and is suitable for generating ultrashort pulse lasers.

optics