Abstract:Concerning the rapid progress in elastic and transparent optoelectronics, the need for cost-effective materials for transparent optoelectronic devices has become a mainstream research trend. Therefore, this report aimed to explore the modifications of the PVA characteristics due to In(acac) 3 doping. New PVA:In(acac) 3 nanocomposite thin films were fabricated using a cost-effective and facile spin-coating technique with varying the In(acac) 3 loading concentration. The structural and molecular feature variations of PVA have been tracked using XRD and FTIR techniques, respectively. Furthermore, by varying In(acac) 3 's concentration, the fabricated films' linear/nonlinear optical properties have been investigated symmetrically using the UV-visible-NIR spectrophotometric technique. The measured transmittance spectra of the prepared films showed the tunability of the energetic position of the fundamental edge while conserving the high transparency. The energy gap and Urbach energy of the prepared thin films have been calculated as a function of doping concentration. The nonlinear refractive index and optical susceptibilities were estimated for all the fabricated films. On the other hand, the photodetection response of the fabricated Schottky barrier devices was tested. The fabricated devices showed pronounced UV response, where the photocurrent density was significantly enhanced under UV illumination up to 0.1 mA/cm 2 for the 20 wt.% In(acac) 3 doped films. The photodetection performance of the manufactured nanocomposite thin films under repeatable On/Off switching cycles was tested. The optimum doping concertation of In(acac) 3 was determined in terms of the analyzed optical and photodetection characteristics to be 20 wt.%. The obtained results support the careful reconsideration of the possibility of exploiting some cheap polymers as important components in advanced optoelectronic applications.

New Polymeric Nanocomposite Thin Films for Transparent Optoelectronics: Impact of In(acac) 3 on the Structural, Optical and Photoelectrical Characteristics of PVA Films