Preparation and investigation of Zn foil/poly(lactic acid) composite films for guiding bone regeneration

Hong Cai,Hongxing Wang,Yan Zhang,Huafang Li,Bing Han,Jiayue Shang,Yinuo Zheng,Haitao Zhao

DOI: https://doi.org/10.1016/j.surfcoat.2024.131537

IF: 4.865

2024-11-10

Surface and Coatings Technology

Abstract:We prepared Zn/Poly(lactic acid) (PLA) composite films for guiding bone regeneration. The surface of Zn foil was modified by micro-arc oxidation, and the composite films with a sandwich structure were prepared using hot pressing method. The morphology, roughness, porosity, and pore size of Zn foil were investigated with the help of laser microscope and SEM. As a result, the rough and porous surface with the S a value of 2.764±0.071 μm and porosity of 12.5±3.2 % provided a favorable structural basis for subsequent combination between Zn foil and PLA. While the value of S a for the MAO-Zn/PLA40 composite film was 4.510±0.080 μm. The main component of the oxide layer was ZnO according to the XRD and XPS results. The tensile strength of MAO-Zn/PLA40 composite film increased by 17.7±0.6 % compared with that of Zn/PLA40 composite film. The interface energy decreased from −7.074 kcal/mol for Zn/PLA to −1433.430 kcal/mol for ZnO/PLA and the total energy level of ZnO/PLA composites shifted towards lower direction according to the density of state results. These results illustrated the enhanced interfacial bonding effect between the micro-arc oxide layer and PLA based on mechanical interlocking and electrostatic attraction. Additionally, micro-arc oxidation accelerated the degradation of Zn foil from initial 0.383±0.029 mm/year to 1.245±0.208 mm/year according to the electrochemical performances. This investigation provided an experimental basis and theoretical guidance for regulating the mechanical properties and degradation rate of this kind of membrane.

physics, applied,materials science, coatings & films