Abstract:Heterogeneous electrocatalytic reactions only occur at the interface between the electrocatalyst and reactant. Therefore, the active sites are only necessary to be distributed on the surface of the electrocatalyst. Based on this motivation, here, we demonstrate a systematic study on surface tuning for a carbon-based electrocatalyst from metal-free (with the heteroatoms N and S, NS/C) to metal-containing surfaces (with Co, N, and S, CoNS/C). The CoNS/C electrocatalyst was obtained by pyrolyzing the Co precoordinated and p-toluenesulfonate-doped polypyrrole (PPy). It was found that the coordination of Co on the PPy ring tuned the final carbon electrocatalyst into a catalyst with a CoNx moiety-rich surface. In addition, the as-synthesized CoNS/C was determined to have a very high loading of cobalt up to 2.02 wt %. The pyrolysis of the cobalt-containing precursor tends to proceed toward a characteristic of a higher sp2 carbon content, a higher surface area, and more nitrogen as well as active nitrogen sites than its metal-free counterpart. The most distinguished feature for such a catalyst is that the truly most active component is only distributed on the surface, in contrast with that of the conventional metal–N-based catalyst present throughout the bulky structure. Especially, the electrocatalytic activity toward oxygen evolution reaction (OER) has been investigated experimentally and theoretically. The results showed that the OER performance of the carbon-based electrocatalyst was remarkably boosted after the introduction of Co with an overpotential decrease from 678 to 345 mV at 10 mA cm–2. Furthermore, CoNS/C displayed an excellent durability upon a long-term measurement. The apparent activation energy measurements revealed that the metal-rich surface contributed to overcome the energy barrier for OER. In addition, density functional theory calculations have been conducted to explain the correlated OER mechanism. This study is expected to provide an effective strategy for the design and the synthesis of highly active metal–nitrogen-type electrocatalysts with a high metal loading for various electrocatalytic reactions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c17599?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c17599</a>.Raman spectra and XRD patterns of NS/C and CoNS/C; SEM and HR-TEM images of NS/C; XPS survey spectrum of CoNS/C; TGA curves of CoNS/C and etched CoNS/C; calculated mass content of Co according to TGA; survey XPS spectrum and high-resolution C 1s, N 1s, and S 2p of NS/C; N2 sorption isotherms and BJH desorption pore size distributions of NS/C and CoNS/C; RRDE measurement of the Co–PPy electrode toward OER; LSV curves of CoNS/C electrocatalysts synthesized with various temperatures toward OER; content of N determined using XPS spectra in CoNS/C with different pyrolysis temperatures; fitted parameters for EIS results; LSV curves of CoNS/C and etched CoNS/C toward OER; summary of the overpotentials of the various electrodes at 10 mA cm–2; temperature-dependent LSV curves of the corresponding fittings of activation energy of NS/C, CoNS/C, and RuO2 toward OER; ADT tests of NS/C toward OER; SEM image of CoNS/C and NS/C after the ADT test; survey XPS spectrum and high-resolution N 1s and Co 2p of CoNS/C after the test; DFT calculations; and summary of the OER activity comparison for recent various advanced non-precious-metal-based electrocatalysts (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17599/suppl_file/am0c17599_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Selective surface nitridation of the self-supported Co oxide nanobushes catalytic electrode towards efficient oxygen evolution reaction

Enhanced Oxygen Evolution Reaction Performance on NiSx@Co3O4/Nickel Foam Electrocatalysts with Their Photothermal Property.

Defective Layered NiFe Double Hydroxides Anchored on Self-Supported CoNi-nitrogen Doped Carbon Nanotube Composite As Advanced Electrocatalyst for Oxygen Evolution Reaction

Facilitating interface charge transfer via constructing NiO/NiCo 2 O 4 heterostructure for oxygen evolution reaction under alkaline conditions

In-situ growing low-crystalline Co9S8Ni3S2 nanohybrid on carbon cloth as a highly active and ultrastable electrode for the oxygen evolution reaction

High-Valence-State NiO/Co3O4 Nanoparticles on Nitrogen-Doped Carbon for Oxygen Evolution at Low Overpotential

Porous Cobalt Oxynitride Nanosheets for Efficient Electrocatalytic Water Oxidation

Surface Tuning to Promote the Electrocatalysis for Oxygen Evolution Reaction: From Metal-Free to Cobalt-Based Carbon Electrocatalysts

Surface nitridation of nickel-cobalt alloy nanocactoids raises the performance of water oxidation and splitting

Metallic nickel anchored on amorphous nickel cobalt oxide nanorods as efficient electrocatalysts toward oxygen evolution reaction

Fabrication of NiCo@Ni3S2/Nickel foam electrocatalyst with ultrathin NiCo layered double hydroxide film wrapping Ni3S2 nanoarrays for efficient oxygen evolution reaction

N-doped CoO Nanowire Arrays As Efficient Electrocatalysts for Oxygen Evolution Reaction

Enhancing Oxygen Evolution Reaction Performance: Electrochemical Activation of the Biphasic CoNi/Zn(Fe,Al,Cr) 2 O 4 via Controlled Aluminum Leaching Facilitated Surface Reconstruction

Enhanced electrocatalytic performance for oxygen evolution reaction via active interfaces of Co3O4arrays@FeOx/Carbon cloth heterostructure by plasma-enhanced atomic layer deposition

Trace rare earth modulated tetranickel nitride embedded in mesoporous carbon as electrocatalysts for the oxygen evolution reaction

Synergistic effect of nanocrystalline NiCo 2 S 4 and NiCo alloy embedded in N-doped carbon fibers towards high-performance electrocatalysts for oxygen evolution reaction

Highly exposed NiFeO x nanoclusters supported on boron doped carbon nanotubes for electrocatalytic oxygen evolution reaction

Boosting Electrocatalytic Oxygen Evolution: Superhydrophilic/Superaerophobic Hierarchical Nanoneedle/Microflower Arrays of Ce x Co3- xO4 with Oxygen Vacancies

Fe induced nanostructure reorganization and electronic structure modulation over CoNi (oxy)hydroxide nanorod arrays for boosting oxygen evolution reaction

Boosting Electrocatalytic Oxygen Evolution Using Ultrathin Carbon Protected Iron–cobalt Carbonate Hydroxide Nanoneedle Arrays

Interfacial electronic regulation on NiCo2O4 nanowires@NiFe-LDH nanosheets heterostructure for efficient oxygen evolution