Inkjet Printing of Ag and Polystyrene Nanoparticle Emulsions for the One-Step Fabrication of Hydrophobic Paper-Based Surface-Enhanced Raman Scattering Substrates
Natércia C.T. Martins,Sara Fateixa,Tiago Fernandes,Helena I.S. Nogueira,Tito Trindade
DOI: https://doi.org/10.1021/acsanm.1c00112
IF: 6.14
2021-05-19
ACS Applied Nano Materials
Abstract:Hydrophobic substrates for surface-enhanced Raman scattering (SERS) of adsorbate species are of great interest in chemical analysis because they can concentrate the analyte molecules in a small area of the surface, thereby improving the SERS sensitivity. Here, we propose a general strategy to fabricate hydrophobic paper-based substrates for SERS applications. The paper substrates have been manufactured by inkjet printing of aqueous emulsions containing Ag and polystyrene (PS) colloidal nanoparticles. In a first stage, the SERS performance of the substrates was optimized by varying the relative amounts of polymer/metal colloidal nanoparticles, the number of printing layers, and the degree of hydrophobicity of the substrates, using crystal violet as a molecular probe, which is well known for its strong SERS activity. In these conditions, the strongest surface Raman enhancement was observed for the highest water contact angle (146°) achieved. The selected Ag/PS-coated paper substrates showed wide applicability for several analytes, but in this study, a detailed analysis is provided for the pesticide thiram as a proof of concept. Several samples spiked with thiram have been analyzed by SERS, giving a detection limit of 0.024 ppm thiram in mineral water and apple juice, while in apple peel, the detection limit achieved for the same pesticide was 600 ng/cm<sup>2</sup>. We suggest that this one-step fabrication method produces a hydrophobic coating whose nanoscale features improve the SERS performance of the paper substrates.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.1c00112?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.1c00112</a>.Photograph of Ag/PS inkjet-printed SERS substrates; STEM image of Ag NPs and digital photograph of Ag NP colloid; STEM image of PS NPs and the digital photograph of PS NP emulsion; EDS spectrum of paper substrates printed with 20 layers of ink Ag16×_PS 0.6; SEM images of paper substrates printed with 20 layers of inks Ag5×_PS 0.6, Ag10×_PS 0.6, Ag16×_PS 0.6, Ag33×_PS 0.6, and 30 layers of ink Ag16×_PS 0.6; AFM images of non-coated office paper and coated office paper using ink formulation Ag16×_PS 0.6; Raman spectra of CV aqueous solution, Raman spectra of office paper with CV and of office paper printed with PS (0.6%) with CV; Raman spectra of substrates printed with Ag/PS ink; intensity of the band at 1620 cm<sup>–1</sup> in the SERS spectrum of CV, for Ag/PS substrates printed with ink Ag16×_PS 0.6 on office paper or filter paper (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.1c00112/suppl_file/an1c00112_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology