Impact of fast-solidification on all- d -metal NiCoMnTi based giant magnetocaloric Heusler compounds

Fengqi Zhang,Ziying Wu,Jianlin Wang,Wenyu Chen,Zhenduo Wu,Xiang Chi,Chenglong Zhao,Stephan Eijt,Henk Schut,Xuedong Bai,Yang Ren,Niels van Dijk,Ekkes Brück

DOI: https://doi.org/10.1016/j.actamat.2023.119595

IF: 9.4

2023-12-12

Acta Materialia

Abstract:Recently, the all- d -metal Ni(Co)MnTi based Heusler compounds are found to have a giant magnetocaloric effect (GMCE) near room temperature and manifest different functionalities like multicaloric effects, which can be employed for solid-state refrigeration. However, in comparison to other traditional Heusler compounds, the relatively large thermal hysteresis ( ΔT hys ) and moderately steep ferromagnetic phase transition provides limitations for real applications. Here, we present that fast solidification (suction casting) can sufficiently tailor the GMCE performance by modifying the microstructure. Compared with the arc-melted sample, the magnetic entropy change of the suction-casted sample shows a 67 % improvement from 18.4 to 29.4 Jkg −1 K −1 for a field change (∆ μ 0 H ) of 5 T. As the thermal hysteresis has maintained a low Δ T hys value (5.5 K) for the enhanced first-order phase transition, a very competitive reversible magnetic entropy change of 21.8 Jkg −1 K −1 for ∆ μ 0 H = 5 T is obtained. Combining high-resolution transmission electron microscopy (HRTEM) and positron annihilation spectroscopy (PAS) results, the difference in lattice defect concentration is found to be responsible for the significant improvement in GMCE for the suction-cast sample, which suggests that defect engineering can be applied to control the GMCE. Our study reveals that fast solidification can effectively regulate the magnetocaloric properties of all- d -metal NiCoMnTi Heusler compounds without sacrificing Δ T hys .

materials science, multidisciplinary,metallurgy & metallurgical engineering