Abstract:Ceramic coatings with aluminum titanuate (Al2TiO5) were prepared on Ti–6Al–4V alloy using pulsed bi-polar Micro-arc Oxidation (MAO). The micromorphology and phase composition of the micro-arc-oxidition ceramic coatings on the titanium alloy were characterized by X-ray powder diffraction (XRD), and scanning electron microscopy (SEM) respectively. The results revealed that the distinct discharge channels and pores on the surface of the micro-arc-oxidition coatings appeared, and these channels were connected in the molten state. The electrolyte concentration was inversely proportional to the coating hardness; additionally, the coating prepared with sodium aluminate and sodium hypophosphite concentrations of 4 g/L and 0.5 g/L, respectively, was the most refined after high-temperature sintering, and it was demonstrated to better prevent oxidation. Increasing the electrolyte concentration coincided with fluctuating coating thermal shock resistance. The thermal shock resistance of the coating respectively prepared with sodium aluminate, and the sodium hypophosphite concentrations of 4 g/L and 0.5 g/L was the highest. Additionally, the high-concentration coatings performed significantly better than the low-concentration coatings. The oxidation resistance of the coating samples was also significantly higher than that of the TC4 titanium alloy substrate. The adhesion strength between the coatings and the substrate with and without the sealing treatment was measured by tensile tests. Then, the high-temperature oxidation performance of the coating samples with and without the sealing treatment was investigated by conducting a high-temperature oxidation experiment at a calcinating temperature of 500 °C. The results indicate that the adhesion strength between the coatings and substrate was high for the as-prepared and sealed micro-arc oxidation samples regardless of whether they were calcined. The high-temperature oxidation mass increase curves for the sealed and unsealed coating samples calcined at 500 °C for 500 h revealed that the high-temperature-oxidation-induced mass increase of the coating samples sealed with a sodium silicate solution was much lower than that of the titanium alloy substrate. Thus, the sealing treatment significantly improved the high-temperature oxidation resistance of the TC4 titanium alloy. Lastly, the high-temperature oxidation behavior at 500 °C was analyzed and discussed.

Influences of Sr(OH)2 on the Structure and Corrosion Resistance of Micro‐Arc Oxidation Coatings Formed on TC4 Titanium Alloy

Effect of Oxidation Time on the Structure and Properties of Ti-25Nb-3Zr-2Sn-3Mo Titanium Alloy Microarc Oxide Film Layer

Surface Damage Mitigation Of Tc4 Alloy Via Micro Arc Oxidation For Oil And Gas Exploitation Application: Characterizations Of Microstructure And Evaluations On Surface Performance

Effect of cobalt oxide on characteristics of micro‐arc oxidation coatings on TC11 alloy

Study on Preparation of Micro-Arc Oxidation Film on TC4 Alloy with Titanium Dioxide Colloid in Electrolyte

Influence of Electrolytes on the Microstructure of Microarc Oxidation Coatings on Ti—6Al—4V Alloy

Study on the wear resistance of micro-arc-oxidised ceramic films on the surface of TC4 titanium alloy oil well tubing in the Ordos Basin

Growth characteristics and properties of micro-arc oxidation coating on SLM-produced TC4 alloy for biomedical applications

Characterization of Oxide Coatings Deposited on Pure Titanium by Alternating-Current Microarc Discharge in Electrolyte

Composition and Phase Structure of Microarc Oxidation Coatings Deposited on TA2 Pure Titanium

Preparation of Micro-Arc Oxidation Coating on TC11 Titanium Alloy and Study on Its Microstructure and Performance

Characterization of Microarc Oxidation Coatings on Pure Titanium

Effect of the Microstructure of a Titanium Alloy Fabricated Using Selective Laser Melting on Microarc Oxidation Film

Correlations Between the Growth Mechanism and Properties of Micro-Arc Oxidation Coatings on Titanium Alloy: Effects of Electrolytes

Preparation and Wear Resistance of Porous TC4 Titanium Alloy Micro‐arc Oxidation Coating Produced by Selective Laser Melting

Corrosion and wear properties of micro-arc oxidation treated Ti6Al4V alloy prepared by selective electron beam melting

High‐temperature oxidation resistance and antifailure mechanism of MAO‐SG composite coating on TC4 titanium alloy

Corrosion behavior and mechanism of MAO coated Ti6Al4V with a grain-fined surface layer

Improvement of Oxidation Resistance of TC4 Alloy by Microarc Oxidation with Sol-Gel SiO2 Sealing

Mechanistic analysis of improving the corrosion performance of MAO coatings on Ti-6Al-4V alloys by annealing

High-temperature oxidation resistance of ceramic coatings on titanium alloy by micro-arc oxidation in aluminate solution