Effect of Different Cast Moulds on the Microstructure, Texture and Stress Rupture of TC4 Titanium Alloy
Liu Wenjie,Zong Xuewen,Chen Zhen,Yang Yumeng,Yang Xuedong,Lu Bingheng
2020-01-01
Rare Metal Materials and Engineering
Abstract:The effect of different casting moulds on Ti-based alloys such as TC4 is very significant. The microstructures, texture and high -temperature stress rupture of different cast-mould TC4 alloys were investigated by the optical microscopy (OM), scanning electron microscopy (SEM), electron back scattering diffraction (EBSD), and X-ray diffraction (XRD). The persistent fracture behavior of TC4 alloys was studied. The results show that all TC4 alloy samples of different moulds are composed of a phase, fi phase and co phase, and a phase (around 90% in the matrix) is the main phase. Compared with the graphite -moulded TC4 alloy, the ceramic -moulded TC4 alloy is much more beneficial to beta ->alpha phase transition; therefore, the percentage of alpha phase is higher (by around 5.3%) and its average grain size is larger (d(mean)=37.021 mu m) than those of graphite -moulded TC4 alloys, and distribution of grains is relatively uniform and stable. With the increase of alpha phase percentage, the strength of TC4 alloys decreases and the plasticity increases. Simultaneously, the ceramic -moulded TC4 alloy has strong texture and obvious orientation, and the texture type is {11 (2) over bar0}<1<(1)over bar>00> with an angle of 45 degrees along gamma direction, which further verifies that the texture of samples is related to the enhancement of peaks in (100), (002), (101) directions. The stress rupture of ceramic-moulded TC4 alloy samples at high temperature is better than that of graphite -moulded TC4 alloys. At the temperatures of 400, 430, and 460 degrees C, the stress rupture life of the samples which show ductile fracture and dimple appearance in rupture is increased by 1.174%, 15.401%, 6.998%, respectively. In addition, temperature directly affects the high -temperature stress rupture of TC4 titanium alloy. As the temperature increases, the stress fracture life of TC4 titanium alloy gradually decreases.