Abstract:In the present study, an environmentally friendly oil- and water-resistant paper was developed using a holo-lignocellulosic nanofibril (LCNF)-based composite coating. The LCNF was prepared from wheat straw using a biomechanical method. Characterizations of oil- and water-resistant coated paper and the effect of LCNF content on the performance of the coated paper were confirmed by combining contact angle analysis, Cobb 300s, and mechanical performance tests. The results show that the barrier performance and mechanical strength of the coated paper were greatly improved with the increase of LCNF content. The contact angle of oil and water of coated paper containing 50% LCNF were 69° and 78°, respectively, while the contact angle of oil and water of the base paper were only 30° and 20°, respectively. Cobb 300s values reduced from 110 g/m2 to 30 g/m2 when the LCNF content increased from 50% to 90%. Moreover, under the coating amount of 20 g/m2, the tensile strength of the coating paper was 0.980 KN/m, an increase of 10.11% compared with the base paper. The bursting strength reached 701.930 KPa, which was 10.75% higher than the base paper. In short, it is feasible to prepare LCNF from wheat straw, and apply it to produce water-proof and oil-proof paper. The water-proof and oil-proof paper developed in this study not only offers a novel approach to addressing white pollution but also presents a new research avenue for exploring the potential applications of agricultural waste.

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to develop an environmentally - friendly oil - and - water - dual - barrier paper to replace traditional plastic packaging materials. Specifically, the researchers used a lignocellulose nanofibril (LCNF) - based composite coating to prepare this paper. LCNF is prepared from wheat straw by a bio - mechanical method, aiming to improve the waterproof and oil - proof properties of the paper while maintaining good mechanical strength. This method not only provides a new way to solve the white pollution problem, but also explores the potential application value of agricultural waste. ### Main Problems 1. **Development of Environmentally - Friendly Oil - and - Water - Dual - Barrier Paper**: - **Background**: Single - use plastic products are widely used in daily life because of their low cost, corrosion resistance, high strength and waterproof characteristics. However, these plastic products are difficult to degrade in the natural environment, causing serious threats to the ecological environment and human health. - **Objective**: To develop an environmentally - friendly oil - and - water - dual - barrier paper to replace traditional plastic packaging materials and reduce environmental pollution. 2. **Improving the Waterproof and Oil - proof Properties of the Paper**: - **Method**: Use the lignocellulose nanofibril (LCNF) - based composite coating extracted from wheat straw to enhance the waterproof and oil - proof properties of the paper. - **Effect**: Studies have shown that as the LCNF content increases, the barrier properties and mechanical strength of the coated paper are significantly improved. For example, the oil contact angle and water contact angle of the coated paper containing 50% LCNF are 69° and 78° respectively, while those of the base paper are only 30° and 20°. 3. **Maintaining Good Mechanical Properties**: - **Testing**: Evaluate the performance of the coated paper through contact angle analysis, Cobb 300s test and mechanical property test. - **Results**: When the LCNF content increases from 50% to 90%, the Cobb 300s value decreases from 110 g/m² to 30 g/m². In the case of a coating amount of 20 g/m², the tensile strength of the coated paper is 0.980 KN/m, which is 10.11% higher than that of the base paper; the bursting strength reaches 701.930 KPa, which is 10.75% higher than that of the base paper. ### Keywords - Lignocellulose nanofibril (LCNF) - Oil - proof - Waterproof - Coating - Wrapping paper ### Summary This research has successfully developed an environmentally - friendly oil - and - water - dual - barrier paper using an LCNF - based composite coating, which not only improves the waterproof and oil - proof properties of the paper, but also maintains good mechanical strength. This achievement provides new ideas for solving the white pollution problem and shows the application potential of agricultural waste in the field of environmental protection materials.

Preparation of Environmentally Friendly Oil- and Water-Resistant Paper Using Holo-Lignocellulosic Nanofibril (LCNF)-Based Composite Coating

Cellulose nanofibrils/polydimethylsiloxane double-layer coating for fabrication of high barrier and excellent water- and oil-resistance paper

Development of Multifunctional Paper Using Lignocellulosic Nanofiber-Reinforced Coatings

Fabrication of water/oil-resistant paper by nanocellulose stabilized Pickering emulsion and chitosan

Paper-Based Oil Barrier Packaging using Lignin-Containing Cellulose Nanofibrils

Plastic-free, oil- and water-resistant paper for food packing

Paper material coated with soybean residue nanocellulose waterproof agent and its application in food packaging

Multivalent Metal Ion Cross-Linked Lignocellulosic Nanopaper with Excellent Water Resistance and Optical Performance

Preparation and Characterization of Degradable Cellulose−Based Paper with Superhydrophobic, Antibacterial, and Barrier Properties for Food Packaging

Water and oil-resistant paper materials based on sodium alginate/hydroxypropyl methylcellulose/polyvinyl butyral/nano-silica with biodegradable and high barrier properties

All-biomass-based eco-friendly waterproof coating for paper-based green packaging

Cellulose nanofibers/polyvinyl alcohol blends as an efficient coating to improve the hydrophobic and oleophobic properties of paper

Exploiting the Properties of Non-Wood Feedstocks to Produce Tailorable Lignin-Containing Cellulose Nanofibers

Lignocellulose Enabled Highly Transparent Nanopaper with Tunable Ultraviolet-Blocking Performance and Superior Durability

Facile preparation of Pickering emulsion-based coatings for hydrophobic, oil-resistant, biodegradable green paper-based packaging

Preparation of multi-barrier and multi-functional paper-based materials by chitosan, ethyl cellulose and green walnut husk biorefinery products for sustainable food packaging

Preparation of environmentally friendly hydrophobic paper by coating method

Enhancing barrier and mechanical properties of paper through NMMO/cellulose solution coating

Multifunctional coatings fabricated from Chinese hemp–derived superhydrophobic micro–nanocellulose

Improving Hydrophobicity and Water Vapor Barrier Properties in Paper Using Cellulose Nanofiber-Stabilized Cocoa Butter and PLA Emulsions

Preparation and Performance of Lignin-Based Multifunctional Superhydrophobic Coating