Self-extinguishing and transparent epoxy resin modified by a phosphine oxide-containing bio-based derivative

Gang Tang,Ruiqing Zhao,Dan Deng,Yadong Yang,Depeng Chen,Bing Zhang,Xinliang Liu,Xiuyu Liu
DOI: https://doi.org/10.1007/s11705-021-2042-1
IF: 4.803
2021-04-28
Frontiers of Chemical Science and Engineering
Abstract:<p class="a-plus-plus">A phosphine oxide-containing bio-based curing agent was synthesized by addition reaction between furan derivatives and diphenylphosphine oxide. The molecular structure of the as-prepared bio-based curing agent was confirmed by Fourier transform infrared spectroscopy and nuclear magnetic resonance spectroscopy. Dynamic mechanical analysis results indicated that with the increase of bio-based curing agent content, the glass transition temperature of epoxy/bio-based curing agent composites decreased, which was related to the steric effect of diphenylphosphine oxide species that possibly hinder the curing reaction as well as the reduction in the cross-linking density by mono-functional N-H. By the addition of 7.5 wt-% bio-based curing agent, the resulting epoxy composite achieved UL-94 V-0 rating, in addition to limiting oxygen index of 32.0 vol-%. With the increase of content for the bio-based curing agent, the peak of heat release rate and total heat release of the composites gradually decreased. The bio-based curing agent promoted the carbonization of the epoxy matrix, leading to higher char yield with good thermal resistance. The high-quality char layer served as an effective barrier to retard the diffusion of decomposition volatiles and oxygen between molten polymers and the flame. This study provides a renewable strategy for fabricating flame retardant and transparent epoxy thermoset. </p>
engineering, chemical
What problem does this paper attempt to address?
The problem this paper attempts to address is improving the flame retardancy of epoxy resin (EP). Although epoxy resin is widely used in advanced resin-based composite materials due to its good adhesion, mechanical properties, chemical stability, low shrinkage, and ease of processing, it also has the drawbacks of being flammable and having poor char-forming properties. These limitations restrict its application in fields requiring high flame retardancy, such as aviation, railway transportation, and electronic and electrical equipment. Therefore, improving the flame retardancy of epoxy resin is crucial for its broader application. Specifically, the paper synthesizes a bio-based curing agent containing phosphorus-oxygen groups (DPO-FD) and adds it to epoxy resin to enhance its flame retardancy. The main objectives of the study include: 1. **Synthesis and characterization of DPO-FD**: Synthesizing DPO-FD through the addition reaction of furan derivatives and diphenyl phosphine oxide, and confirming its molecular structure through Fourier transform infrared spectroscopy (FTIR) and nuclear magnetic resonance spectroscopy (NMR). 2. **Evaluating the impact of DPO-FD on the thermomechanical properties of epoxy resin**: Studying the effect of DPO-FD on the glass transition temperature (Tg) and storage modulus (E') of epoxy resin composites through dynamic mechanical analysis (DMA). 3. **Evaluating the impact of DPO-FD on the thermal decomposition behavior of epoxy resin**: Investigating the effect of DPO-FD on the thermal decomposition temperature and char yield of epoxy resin composites through thermogravimetric analysis (TGA). 4. **Evaluating the impact of DPO-FD on the flame retardancy of epoxy resin**: Assessing the flame retardancy of epoxy resin composites through the limiting oxygen index (LOI) test and UL-94 vertical burning test. 5. **Evaluating the impact of DPO-FD on the combustion process of epoxy resin**: Studying the effect of DPO-FD on the heat release rate (HRR), total heat release (THR), and mass loss of epoxy resin composites through cone calorimeter experiments. Through these studies, the paper aims to provide a renewable strategy for preparing flame-retardant and transparent epoxy thermosetting materials.