Abstract:A series of photocatalysts was synthesized by codoping TiO2 with lanthanum and iodine (La-I-TiO2). The structure and properties of the catalysts were studied by X-ray diffraction (XRD), the Brunauer-Emmett-Teller (BET) method, transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and UV-vis diffuse reflectance spectra. The prepared anatase-phase La-I-TiO2 (molar ratio 20:20:100) calcined at 400 degrees C had a BET surface area of 92.9 m(2) g(-1), and the crystallite size calculated from XRD data was similar to 3.57 nm, and it had a remarkable absorption in the visible light range of 400-550 nm. The catalytic efficiency was tested by monitoring the photocatalytic degradation of oxalic acid under visible light irradiation. An optimum molar ratio of 20:100 La/TiO2 was determined for the most efficient inhibition of the recombination of electron-hole pairs and the photocatalytic activity of La-I-TiO2 calcined at 400 degrees C was significantly higher than that calcined at 500 or 600 degrees C in aqueous oxalic acid solution. The probable process of oxalic acid degradation was that it was first adsorbed onto the surface of the catalysts, where it reacted with valence band holes (h(vb)(+)) and the surface-bound or adsorbed (OH)-O-center dot radicals ((OHads)-O-center dot) as well as reactive oxygen species (ROS) derived from oxygen reduction by photogenerated electrons, and finally converted into CO2 and H2O without any stable intermediate.

Assessment of CO2 photoconversion over TiO2/La2O3 treated with acetic acid

A Visible Light-Driven Titanium Dioxide Photocatalyst Codoped with Lanthanum and Iodine: an Application in the Degradation of Oxalic Acid

Promotional effect of Ti doping on the ketonization of acetic acid over a CeO2 catalyst

Tuning the Photoelectronic and Photocatalytic Properties of Single-Crystalline TiO 2 Nanosheet Array Films with Dominant {001} Facets by Controlling the Hydrochloric Acid Concentration

Acidification of La loaded TiO2 for photocatalytic conversion of CO2

Sol-Gel Preparation and Characterization of Activated Carbon Supported TiO_2 Photocatalyst

Photothermal Catalysis for Selective CO2 Reduction on the Modified Anatase TiO2 (101) Surface

TiO2 Modification with Transition Metallic Species (Cr, Co, Ni, and Cu) for Photocatalytic Abatement of Acetic Acid in Liquid Phase and Propene in Gas Phase

Photocatalytic Reduction of CO 2 with Water Vapor on Surface La-modified TiO 2 Nanoparticles with Enhanced CH 4 Selectivity

Self-doped TiO2 Nanotubes with Surface Modification by Ionic Liquids for Enhanced Photoreduction of CO2 to Acetic Acid

Bi‐, Y‐Codoped TiO2 for Carbon Dioxide Photocatalytic Reduction to Formic Acid under Visible Light Irradiation

Preparation and Characterization of Highly Active Mesoporous TiO2 Photocatalysts by Hydrothermal Synthesis under Weak Acid Conditions

Photocatalytic oxidation and decomposition of acetic acid on titanium silicalite

High performance supported photocatalyst of nano-TiO2/activated carbon from metatitanic acid

Ti3+ Self-Doped TiO2 Via Facile Catalytic Reduction over Al(acac)3 with Enhanced Photoelectrochemical and Photocatalytic Activities

Preparation of C Doped TiO2 Photocatalysts and Their Photocatalytic Reduction of Carbon Dioxide

Preparation and Application of Efficient TiO2/ACFs Photocatalyst

Acid-assisted hydrothermal synthesis of nanocrystalline TiO2 from titanate nanotubes: influence of acids on the photodegradation of gaseous toluene.

Acid-assisted Synthesis of TiO2 Nanoparticles for Enhancement of Visible Light Photocatalytic Efficiency

Photocataltic reduction of CO2 by nanometer LaFeO3-TiO2

Influence of sol-gel and dip-hydrothermal preparation methods on structure and performance of TiO2/AC photocatalysts