Capacity Enhancement of Porous Carbon Electrodes during Long-Term Cycling in Lithium-Ion Batteries

Yaxin Chen,Liluo Shi,Ang Li,Su Zhang,Mengyao Guo,Xiaohong Chen,Jisheng Zhou,Huaihe Song

DOI: https://doi.org/10.1149/2.1151709jes

IF: 3.9

2017-01-01

Journal of The Electrochemical Society

Abstract:Capacity enhancements are sometimes observed when carbon materials, especially porous carbons, are used as lithium-ion batteries anodes. However, the correlative mechanism is unclear now. Here, porous carbon (PC) is used to reveal the mechanism by using a combination of structure analysis and electrochemical calculations. The coexistence of blind pores and closed pores with fractal porous structure is confirmed by N2 sorption and small angle X-ray scattering. When the PC with main pore diameter of 30 nm is used as lithium-ion batteries anode, the specific capacity increases from 700 mAh g−1 (40th cycle) to 1300 mAh g−1 (110th cycle) at a current density of 50 mA g−1. It could be ascribed to the stepwise diffusion of Li atoms inside the pore structure, including the following two effects. (1) The diffusion of solvated Li+ in the blind pores results in the continuous formation of solid electrolyte interface, providing more activated sites on the inside surface; (2) Li atoms diffuse into the inner closed pores via disordered carbon walls to further enhance the reversible capacity. Our finding provides a deep insight on the mechanism of capacity enhancement of porous carbon electrodes, which could benefit the design of advanced electrode materials.

electrochemistry,materials science, coatings & films