Abstract:The efficient ethanol electrosynthesis from CO2 is challenging with low selectivity at high CO2 electrolysis rates, due to the competition with H2 and other reduction products. Copper-based bimetallic electrocatalysts are potential candidates for the CO2-to-ethanol conversion, but the secondary metal has mainly been focused on active components (such as Ag, Sn) for CO2 electroreduction, which also promote selectivity of ethylene or other reduction products rather than ethanol. Limited attention has been given to alkali-earth metals due to their inherently active chemical property. Herein, we rationally synthesized a (111) facets-oriented nano Cu2Mg (designated as Cu2Mg(111)) intermetallic compound with high-density ordered Cu3-Mg sites. The in-situ Raman spectroscopy and density function theory calculations revealed that the Cu3ẟ−-Mgẟ+ active sites allowed to increase *CO surface coverage, decrease reaction energy for *CO–CO coupling, and stabilize the *CHCHOH intermediates, thus promoting the ethanol formation pathway. The Cu2Mg(111) catalyst showed a high FEC2H5OH of 76.2 ± 4.8% at 600 mA·cm-2, and a peak value of |jC2H5OH| of 720 ± 34 mA·cm-2, almost 4 times of that using conventional Cu2Mg with (311) facets, comparable to the best reported values for the CO2-to-ethanol electroreduction.

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to improve the selectivity and efficiency of electro - reduction of carbon dioxide (CO\(_2\)) to ethanol (C\(_2\)H\(_5\)OH). Specifically, the authors developed a nano - Cu\(_2\)Mg intermetallic compound catalyst with a specific (111) crystal - face orientation. This catalyst can efficiently convert CO\(_2\) into ethanol at industrial current densities. ### Main research background and problems 1. **Challenges in electro - reduction of CO\(_2\)**: - Currently, the Faraday efficiency (FE) of electro - reduction of CO\(_2\) to ethanol is usually less than 40%, especially at high electrolysis rates (> 1 A·cm\(^{-2}\)). - Although traditional Cu - based catalysts can achieve C - C coupling to produce multi - carbon (C\(_2^+\)) products, these catalysts will also produce other by - products such as methane (CH\(_4\)) and ethylene (C\(_2\)H\(_4\)) while producing ethanol, which reduces the selectivity of ethanol. 2. **Design of bimetallic catalysts**: - By alloying Cu with other metals to construct bimetallic materials, the adsorption energy of intermediates can be adjusted, thereby improving the selectivity of specific products. - However, most studies focus on active metal elements (such as Au, Ag, Sn, etc.), which mainly promote the production of CO, formate or ethylene, rather than ethanol. - There is less attention on alkaline - earth metals (such as Mg) because they are easily reactive in water or air. ### Solutions 1. **Preparation of Cu\(_2\)Mg(111) catalyst**: - The authors successfully prepared nano - Cu\(_2\)Mg intermetallic compounds with (111) crystal - face orientation by heat - treating commercial Cu and Mg powders dispersed in carbon black. - This catalyst has a high - density of ordered Cu\(_3\)-Mg sites, and electrons transfer from Mg to Cu to form Cu\(_3^\delta^-\)-Mg\(^{\delta^+}\) active sites. 2. **Performance testing**: - Compared with the traditional Cu\(_2\)Mg (311) crystal - face, the Cu\(_2\)Mg(111) catalyst has an ethanol Faraday efficiency of 76.2 ± 4.8% at a total current density of 600 mA·cm\(^{-2}\), and the partial current density reaches 720 ± 34 mA·cm\(^{-2}\), which is much higher than that of the traditional Cu\(_2\)Mg catalyst. - The stability and selectivity of the catalyst at high current densities have also been verified. ### Conclusion By rationally designing the Cu\(_2\)Mg intermetallic compound catalyst with (111) crystal - face orientation, the authors have successfully improved the selectivity and efficiency of electro - reduction of CO\(_2\) to ethanol. This result provides a new strategy for efficient electro - synthesis of ethanol, especially having important significance in industrial applications.

(111) Facet‐oriented Cu2Mg Intermetallic Compound with Cu3‐Mg Sites for CO2 Electroreduction to Ethanol with Industrial Current Density

Over 2 A Cm-2 CO2-to-Ethanol Conversion by Alkali-Metal Cation Induced Copper with Dominant (200) Facets

Selective CO2Electroreduction to Ethanol over a Carbon‐Coated CuOxCatalyst

Synergistic Effect of Cu2 O Mesh Pattern on High-Facet Cu Surface for Selective CO2 Electroreduction to Ethanol

Enhancement of electrocatalytic CO 2 performance by different components of Cu-based bimetallic MOFs

Critical Role of Cu Nanoparticle-Loaded Cu(100) Surface Structures on Structured Copper-Based Catalysts in Boosting Ethanol Generation in CO2 Electroreduction

Selective Increase in CO2 Electroreduction to Ethanol Activity at Nanograin‐Boundary‐Rich Mixed Cu(I)/Cu(0) Sites via Enriching Co‐Adsorbed CO and Hydroxyl Species

Highly selective electrocatalytic CO2 reduction to ethanol by metallic clusters dynamically formed from atomically dispersed copper

Boosting electrocatalytic CO2–to–ethanol production via asymmetric C–C coupling

Ampere-Level CO 2 -to-Ethanol Conversion via Boron-Incorporated Copper Electrodes

Multivalent Cu sites synergistically adjust carbonaceous intermediates adsorption for electrocatalytic ethanol production

Electron‐Deficient Cu Sites on Cu3Ag1 Catalyst Promoting CO2 Electroreduction to Alcohols

Enhanced interfacial effect-induced asymmetric coupling boost electroreduction of CO 2 to ethylene

Surface Co-Modification of Halide Anions and Potassium Cations Promotes High-Rate CO2-to-Ethanol Electrosynthesis

Highly dispersive trace silver decorated Cu/Cu2O composites boosting electrochemical CO2 reduction to ethanol

Tailoring the Surface and Interface Structures of Copper‐Based Catalysts for Electrochemical Reduction of CO 2 to Ethylene and Ethanol

Asymmetrically Coordinated Cu Dual‐Atom‐Sites Enables Selective CO2 Electroreduction to Ethanol

In situ dual doping for constructing efficient CO2-to-methanol electrocatalysts

Facet‐Selective Deposition of Ultrathin Al2O3 on Copper Nanocrystals for Highly Stable CO2 Electroreduction to Ethylene

Regulated Surface Electronic States of CuNi Nanoparticles through Metal‐Support Interaction for Enhanced Electrocatalytic CO2 Reduction to Ethanol

Metal-Organic Framework Supported Low-Nuclearity Cluster Catalysts for Highly Selective Carbon Dioxide Electroreduction to Ethanol