Biomimetic Brushlike Slippery Coatings with Mechanically Robust, Self-Cleaning, and Icephobic Properties
Yi Tian,Yibin Liu,Zhengzhou Su,Shenqiang Wang,Baoliang Zhang,Hepeng Zhang,Qiuyu Zhang
DOI: https://doi.org/10.1021/acsami.0c14042
2020-11-17
Abstract:In this work, a facile strategy was proposed to prepare a series of brushlike thermoplastic polyurethane (TPU) coatings with mechanically robust, self-cleaning, and icephobic performance. Through a simple multicomponent click reaction of thiolactone with a diamine compound and mono-ethenyl-terminated polydimethylsiloxane (mono-ethenyl-PDMS), a diol with amide groups and flexible PDMS was synthesized, and a novel TPU could be obtained productively by a reaction of isocyanate and diol. The unique chain structure endowed TPU films with ascendant self-stratifying properties. During solvent vapor annealing, flexible PDMS chains migrated and enriched to the surface while urethane linkages with a strong interaction tended to locate at the substrate. Based on this, TPU-PDMS films exhibited mechanically robust property, and the tensile strength value of TPU-PDMS-3 showed a sharp increase to 48.62 MPa. The resultant TPU-PDMS-10 coatings exhibited a water repellent behavior and possessed superior movability of droplet water, and also the dirt on it could be readily removed by rinsing with water without leaving any traces. Furthermore, three different criteria were used to characterize the icephobic performance. The coatings exhibited a significantly lower freezing point (approximately −27 °C) of supercooled water, longer delay-icing time, and less ice adhesion shear strength. Therefore, these novel brushlike TPU coatings have tremendous potential applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c14042?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c14042</a>.Tensile strength and elongation at break of the TPU coating (Table S1), <sup>1</sup>H-NMR spectra, XPS spectra, AFM topography images and phase images, TGA curves, optical picture of the contact angle, self-cleaning test photos, τ<sub>ice</sub> of icing/deicing circles, CAs and SAs, Paints and varnishes—cross-cut test, self-cleaning experiment, and GPC (Figure S1–14) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c14042/suppl_file/am0c14042_si_001.pdf">PDF</a>).Movability of droplet water on TPU-PDMS-10 (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c14042/suppl_file/am0c14042_si_002.mp4">MP4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology