Multistimuli Responsive Solid-State Emission of a Zinc(II) Complex with Multicolour Switching

Han-Wen Zheng,Min Wu,Dong-Dong Yang,Qiong-Fang Liang,Jia-Bin Li,Xiang-Jun Zheng
DOI: https://doi.org/10.1021/acs.inorgchem.1c01586
IF: 4.6
2021-07-21
Inorganic Chemistry
Abstract:The development of smart luminescent materials, especially those stimulus-responsive fluorescent materials that can switch between different colors repeatedly under external stimulation based on a single molecule, is of great significance but a challenge. In this work, a novel zinc(II)–Schiff base complex (ZnL<sub>2</sub>) was obtained and characterized. Upon exposure to the HCl and NH<sub>3</sub> vapors, it displayed remarkable tricolor acidochromic behavior with high contrast and rapid response under the ambient light as well as UV light (365 nm). The XPS analyses of ZnL<sub>2</sub> crystals before and after HCl/NH<sub>3</sub> fuming show that the acidochromism originates principally from the adsorption of vapor and the gas–solid reaction equilibrium on the crystal surface. The reddish-brown color of the HCl-fumigated ZnL<sub>2</sub> crystals could be attributed to the generation of HL at the surface of ZnL<sub>2</sub>, and red-shifted emission could be ascribed to the self-absorption effect. The single crystal X-ray diffraction data indicate that these processes cause slight changes in the molecular conformation and crystal packing. ZnL<sub>2</sub> shows reversible mechanochromic luminescence behavior between yellow and orange emission during the grinding–fuming/heating cycles due to the modulation between amorphous and crystalline states. Moreover, ZnL<sub>2</sub> was successfully made into test paper for the rapid detection of HCl/NH<sub>3</sub> vapors and mechanical stimuli.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.inorgchem.1c01586?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.inorgchem.1c01586</a>.Figure S1 shows multiple intermolecular interactions in ZnL<sub>2</sub>; Figure S2 shows fluorescence decay curves and fit results <b>(</b>excited at 371.8 nm<b>)</b> of ZnL<sub>2</sub> in different states; Figure S3 shows fluorescence spectra of ZnL<sub>2</sub>–HCl and ZnL<sub>2</sub>–HCl–NH<sub>3</sub> in crystal state; Figure S4 shows fluorescence emission spectra of ZnL<sub>2</sub> samples fumigated by NH<sub>3</sub> and HCl after several cycles; Figure S5 shows PXRD patterns, DSC curves of the original crystals and upon HCl/NH<sub>3</sub> fumed samples, and TG curve of the original crystals; Figure S6 shows normalized absorption spectra in THF of HL and ZnL<sub>2</sub> before and after the fumigation of HCl/NH<sub>3</sub> vapor; Figure S7 shows fluorescence emission spectra of HL and the samples exposed to HCl/NH<sub>3</sub> vapor; Figure S8 shows XPS spectra; Figure S9 shows schematic of the ZnL<sub>2</sub>–HCl transformation process fumed by EtOH, and fluorescence emission spectra of the EtOH immersed; Figure S10 shows UV–vis absorption spectra of the original crystals of ZnL<sub>2</sub> and the samples exposed to HCl/NH<sub>3</sub> vapor; Figure S11 shows multiple intermolecular interactions and molecular packing in ZnL<sub>2</sub>–HCl, ZnL<sub>2</sub>–HCl–NH<sub>3,</sub> and ZnL<sub>2</sub>–NH<sub>3</sub>; Figure S12 shows fluorescence emission spectra of ZnL<sub>2</sub> upon repeating the grinding-fuming processes; Figure S13 shows DSC curves of ZnL<sub>2</sub> samples; Figure S14 and Figure S15 show the MCL properties and PXRD patterns of ZnL<sub>2</sub>–HCl, ZnL<sub>2</sub>–HCl–NH<sub>3</sub>, and ZnL<sub>2</sub>–NH<sub>3</sub>; Figure S16 shows fluorescence emission spectra and PXRD patterns of the HL before and after grinding; Table S1 and Table S2 show crystal data and structure refinement parameters of HL and ZnL<sub>2</sub> in different states; Table S3 shows selected bond distance (Å) and angles (deg) of ZnL<sub>2</sub>; Table S4 shows types of intermolecular interactions; Table S5 shows dihedral angles of ZnL<sub>2</sub>; Table S6 shows detailed photophysical properties of ZnL<sub>2</sub> in different states; Table S7 shows dihedral angles of HL<sub>2</sub> (<a class="ext-link" href="/doi/suppl/10.1021/acs.inorgchem.1c01586/suppl_file/ic1c01586_si_001.pdf">PDF</a>)Movie S1 shows reversible color changes and rapid response of ZnL<sub>2</sub> test paper fuming with HCl and NH<sub>3</sub> (<a class="ext-link" href="/doi/suppl/10.1021/acs.inorgchem.1c01586/suppl_file/ic1c01586_si_002.mp4">MP4</a>)This article has not yet been cited by other publications.
chemistry, inorganic & nuclear
What problem does this paper attempt to address?
The paper aims to address the issue of multi-stimuli responsive fluorescent materials, specifically by developing a zinc(II) Schiff base complex (ZnL2) capable of multicolor switching under external stimuli. Specifically, the research objectives include: 1. **Developing novel fluorescent materials**: By synthesizing a new zinc(II) Schiff base complex ZnL2 and studying its fluorescence variation characteristics under acid, base, and mechanical stimuli. 2. **Multicolor switching performance**: Exploring the tricolor acid chromism behavior exhibited by ZnL2 when exposed to HCl and NH3 vapors and its rapid response capability. 3. **Mechanism study**: Investigating in detail the color change mechanism of ZnL2 under acid-base stimuli, including gas-solid surface reaction equilibrium and changes in lattice structure. 4. **Practical application**: Preparing ZnL2 into test paper for the rapid detection of HCl and NH3 vapors as well as mechanical stimuli, demonstrating its potential application value in the field of sensors. In summary, this research aims to develop a fluorescent material with multi-stimuli responsive characteristics, reveal the underlying mechanisms, and provide a theoretical foundation and technical support for the design of multifunctional chromic materials in the future.