Effects of Electron Irradiation on Resistivity and London Penetration Depth Ofba1−xkxfe2as2…
K Cho,M. Kończykowski,J. A. Murphy,H Kim,M. A. Tanatar,Warren E. Straszheim,Bing Shen,Hao Wen,Ruslan Prozorov
DOI: https://doi.org/10.1103/physrevb.90.104514
2014-01-01
Abstract:Irradiation with 2.5 MeV electrons at doses up to $5.2\ifmmode\times\else\texttimes\fi{}{10}^{19} \mathrm{electrons}/\mathrm{cm}{}^{2}$ was used to introduce pointlike defects in single crystals of ${\mathrm{Ba}}_{1\ensuremath{-}x}{\mathrm{K}}_{x}{\mathrm{Fe}}_{2}{\mathrm{As}}_{2}$ with $x=0.19 ({T}_{c}=14\phantom{\rule{0.16em}{0ex}}\mathrm{K}),0.26 ({T}_{c}=32\phantom{\rule{0.16em}{0ex}}\mathrm{K}), 0.32 ({T}_{c}=37\phantom{\rule{0.16em}{0ex}}\mathrm{K})$, and $0.34 ({T}_{c}=39\phantom{\rule{0.16em}{0ex}}\mathrm{K})$ to study the superconducting gap structure by probing the effect of nonmagnetic scattering on electrical resistivity $\ensuremath{\rho}(T)$ and London penetration depth $\ensuremath{\lambda}(T)$. For all compositions, the irradiation suppressed the superconducting transition temperature ${T}_{c}$ and increased resistivity. The low-temperature behavior of $\ensuremath{\lambda}(T)$ is best described by the power-law function, $\ensuremath{\Delta}\ensuremath{\lambda}(T)=A{(T/{T}_{c})}^{n}$. While substantial suppression of ${T}_{c}$ supports ${s}_{\ifmmode\pm\else\textpm\fi{}}$ pairing, in samples close to the optimal doping, $x=0.26$, 0.32, and 0.34, the exponent $n$ remained high $(n\ensuremath{\ge}3)$, indicating almost exponential attenuation and thus a robust full superconducting gap. For the $x=0.19$ composition, which exhibits coexistence of superconductivity and long-range magnetism, the suppression of ${T}_{c}$ was much more rapid, and the exponent $n$ decreased toward the ${s}_{\ifmmode\pm\else\textpm\fi{}}$ dirty limit of $n=2$. In this sample, the irradiation also suppressed the temperature of structural/magnetic transition ${T}_{\mathrm{sm}}$ from 103 to 98 K, consistent with the itinerant nature of the long-range magnetic order. Our results suggest that underdoped compositions, especially in the coexisting regime, are most susceptible to nonmagnetic scattering and imply that in multiband ${\mathrm{Ba}}_{1\ensuremath{-}x}{\mathrm{K}}_{x}{\mathrm{Fe}}_{2}{\mathrm{As}}_{2}$ superconductors, the ratio of the interband to intraband pairing strength, as well as the related gap anisotropy, increases upon the departure from the optimal doping.