Abstract:The yolk-shell Co3O4@Fe3O4/C nanocomposites with Co3O4 as the core, Fe3O4/C as the shell, and a cavity structure were synthesized by the hard template method. The physical and chemical properties of the composites were characterized by SEM, TEM, XRD, TGA, XPS, BET, and VSM. The specific surface area of yolk-shell Co3O4@Fe3O4/C nanocomposites is 175.9 m(2) g(-1), showing superparamagnetic properties. The yolk-shell Co3O4@Fe3O4/C nanocomposites were used as heterogeneous Fenton catalysts to activate peroxymonosulfate (PMS) to degrade MB, which showed high catalytic degradation performance. The degradation rate of MB reached 100 % within 30 min under the circumstances of the yolk-shell Co3O4@Fe3O4/C nanocomposites dosage of 0.1 g L-1, the PMS dosage of 1.0 g L-1, the initial MB concentration of 100 mg L-1, an initial pH of 5.5, and a temperature of 30 +/- 2 degrees C. The enhanced catalytic performance of the yolk-shell Co3O4@Fe3O4/C nanocomposites can be attributed to the synergistic effect of the two catalytically active materials and the middle cavity. The effects of different operating parameters and co-existing anion species on MB degradation were also investigated. Electron paramagnetic resonance (EPR) analysis and quenching experiments confirmed that the formation of SO4 center dot- in the yolk-shell Co3O4@Fe3O4/C/PMS system contributes to MB degradation. In addition, yolk-shell Co3O4@Fe3O4/C nanocomposites can be easily separated from the pollutant solution under the action of an external magnetic field, and the degradation rate of MB can still reach 98 % after five cycles, indicating that it has good stability and reusability and has broad application prospects in the field of water purification.

Magnetic Fe 3 O 4 @CoFe-LDH nanocomposite heterogeneously activated peroxymonosulfate for degradation of azo-dye AO7

Magnetic Ternary Hybrid Composites as an Efficient Photocatalyst for Degradation of Acid Orange 7 Dye

Heterogeneous Electro-Fenton Oxidation of Azo Dye Methyl Orange Catalyzed by Magnetic Fe3o4 Nanoparticles

Activation of peroxymonosulfate by CoFe2O4 loaded on metal-organic framework for the degradation of organic dye

Yolk-shell Co3 O4 @fe3 O4 /C Nanocomposites As a Heterogeneous Fenton-like Catalyst for Organic Dye Removal.

Magnetic nanoscaled Fe3O4-CeO2-TiO2 composite: UV-Fenton reaction to degrade AO-7 dye

Synthesis of magnetic CoFe2O4/ordered mesoporous carbon nanocomposites and application in Fenton-like oxidation of rhodamine B

Peroxymonosulfate activation by magnetic CoNi-MOF catalyst for degradation of organic dye

MnCo/N-C composite nanomaterials derived from MOFs as peroxymonosulfate activators for highly efficient removal of dyes

Magnetic powder MnO-Fe2O3 composite--a novel material for the removal of azo-dye from water.

Manganese doped magnetic cobalt ferrite nanoparticles for dye degradation via a novel heterogeneous chemical catalysis

Magnetic cobalt nanoparticles embedded in a carbonaceous hydrogel for the activation of peroxymonosulfate to degrade azo dyes and organic pollutants

CuFe2O4/activated Carbon Composite: a Novel Magnetic Adsorbent for the Removal of Acid Orange II and Catalytic Regeneration.

Magnetic Fe/N-codoped carbon derived from modified Fe-base MOFs: Synergism of multiple active sites for peroxymonosulfate activation

A Magnetic CoFe2O4-CNS Nanocomposite As an Efficient, Recyclable Catalyst for Peroxymonosulfate Activation and Pollutant Degradation

Magnetic COFs As Catalyst for Fenton-like Degradation of Sulfamethazine.

Non-radical-dominated catalytic degradation of methylene blue by magnetic CoMoO4/CoFe2O4 composite peroxymonosulfate activators

Magnetic Nitrogen-Doped Fe3C@ c Catalysts for Efficient Activation of Peroxymonosulfate for Degradation of Organic Pollutants

Synthesis of magnetic Fe3O4-HKUST-1 nanocomposites for azo dye adsorption

Magnetic Fe 3 O 4 nanoparticles supported on carbonized corncob as heterogeneous Fenton catalyst for efficient degradation of methyl orange

Ultra-fast magnetic catalytic degradation of organic dyes by the Fe-doped metallic 1T/1T′ MoS 2 nanocomposites