Abstract:The main chemical component of high-silicon iron tailings (HSITs) is SiO2; HSITs also include some oxides such as Al2O3 and CaO. Mechanical activation can reduce the particle size of HSITs and enhance their pozzolanic activity such that they can be used as a type of mineral admixture for cement-based materials (CBMs). This study aims to investigate the mechanical activation (ultrafine grinding) effects of HSITs, including physical and crystallization structure effects. The particle distribution, specific surface area, density, and solubility of HSITs were tested using laser particle size analysis and other routine physical testing methods. Their crystal structures were analyzed using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and differential scanning calorimetry-thermogravimetry (DSC-TG). Grinding reduced the particle size of HSIT particles and increased their specific surface area, wherein the minimum D50 was 5.75 μm, the maximum specific surface area was 7608 m2/kg, and the corresponding grinding time was 3.5 h. With an increase in grinding time, the solubility showed an increasing trend; however, the density showed a decreasing trend. The change was fast before 3.5 h or 4 h and then slowed down, but the final solubility was still higher than its initial level, while the final density was still lower than its initial level. Grinding reduced the degree of crystallization of the minerals in HSITs and increased the microscopic strain and disorder of its crystal structure. These changes were significant for a grinding time of 0–3.5 h, after which the changes tended to be slow. The symmetry and integrity of the SiO2 structure decreased with grinding. The activity index of the HSIT powder was higher than 0.6. Ultrafine grinding improves the particle size distribution of HSITs and reduces the crystallinity of their main minerals, which in turn increases their chemical reactivity. It can be said that ultra-finely ground HSIT powder is pozzolanic and can be used as a mineral admixture for CBMs, and its grinding limit can be inferred to be 3.5 h.

Ultrafine Grinded and Silane Grafted Iron Ore Tailings as Reinforcing Filler of Styrene Butadiene Rubber

Application of Composite Powders Recycled from Graphite Tailings in Styrene-Butadiene Rubber

Mesoporous Spherical Silica Filler Prepared from Coal Gasification Fine Slag for Styrene Butadiene Rubber Reinforcement and Promoting Vulcanization

Performance of Full-Component Coal Gasification Fine Slag: High-Value Utilization as Reinforcing Material in Styrene-Butadiene Rubber (ESBR) for Replacing Carbon Black

Effect of 3-Mercaptopropyltriethoxysilane Modified Illite on the Reinforcement of SBR

Improved Thermal Insulation and Mechanical Strength of Styrene-Butadiene Rubber through the Combination of Filled Silica Aerogels and Modified Glass Fiber

The Mechanical and Viscoelastic Properties of SSBR Vulcanizates Filled with Organically Modified Montmorillonite and Silica

Purification, Surface Modification of Coal Ash Silica and Its Potential Application in Rubber Composites

Structure and Properties of Particles/rubber Composites Applied on Functionally Graded Lapping and Polishing Plate

Effect of silica particle size and coating by natural latex on properties of styrene‐butadiene rubber/carbon black/silica composites

Stabilization of iron ore tailing with low-carbon lime/carbide slag-activated ground granulated blast-furnace slag and coal fly ash

Study of Styrene Butadiene Rubber Reinforced by Polybutadiene Liquid Rubber-Modified Silica

Selective Decomposition of Waste Rubber from the Shoe Industry by the Combination of Thermal Process and Mechanical Grinding

The effects of filling method on silicone rubber composites filled with SiO2 and TiO2

On the Use of Mechano-Chemically Modified Ground Tire Rubber (GTR) as Recycled and Sustainable Filler in Styrene-Butadiene Rubber (SBR) Composites

A green dual-phase carbon-silica nanohybrid derived from black liquor lignin for reinforcing styrene-butadiene rubber

Enhancing mechanical performance and wet‐skid resistance of emulsion styrene butadiene rubber/natural rubber latex composites via in‐situ hybridization of silanized graphene oxide and silica

On the grinding effects of high-silicon iron tailings

The effect of modified carbon black and nano-silica, individually and in combination, on the curing, mechanical, and dynamical properties of butyl rubber (IIR)

Reactive grafting of hydroxyethyl acrylate in styrene butadiene rubber: Characterization and its effect on silica reinforced tire composites

Application of low‐molecular‐weight polyethylene glycol‐modified silica in natural rubber composites