Charge Transfer Enhancement by Substitutional N and NiFeOOH Cocatalyst of N-TiO 2 /NiFeOOH Nanorod Photoanode for Solar Water Splitting

Li Fu,Yimin Lin,Wanqing Fang,Rongzi Xv,Xiaoying Shang

DOI: https://doi.org/10.1016/j.electacta.2023.143137

IF: 6.6

2023-09-06

Electrochimica Acta

Abstract:The increasing demand for renewable and substantial energy has aroused the development of semiconductors for applications in photoelectrochemical (PEC) water splitting. Herein, we demonstrate the synthesis of the nitrogen-doping NiFeOOH modified TiO 2 nanorods (N-TiO 2 /NiFeOOH) as photoanode. The N-TiO 2 /NiFeOOH photoanode has the core-shell structure. The "core" is nitrogen doping TiO 2 nanorods with anatase and rutile phase while the "shell" is NiFeOOH layers. The XPS characterization presents the oxygen vacancy (O v ) increase with the substitutional N sites increase. The trends of applied bias photon-to-current efficiency are agreed with the substitutional N sites and O v atomic content. That infers that the substitutional N sites affect the O v content, which could function as the active sites for the enhanced PEC properties by increase the charge separation/injection efficiencies. After NiFeOOH modification, that leads to an enhanced photocurrent density of 3.61 mA cm −2 for the N-TiO 2 /NiFeOOH photoanode, which is 1.2 and 2.4 times larger than that of the N-TiO 2 and original TiO 2 photoanodes. The enhancement in the PEC performance and efficiency are attribute to the synergetic effect of the substitutional N doping for the defect modulation and NiFeOOH modification for the oxygen evolution reaction kinetics promotion, thus enhance the charge separation/injection efficiencies at the interface between the N-TiO 2 /NiFeOOH photoanode and the electrolyte.

electrochemistry