Copper (II)‐azo sulfathiazole complex immobilized on UiO‐66‐NH2 (MOF) as a catalyst for the one‐pot synthesis of spiroindole‐pyranopyrazoles

Leila Ghasempour,Sakineh Asghari

DOI: https://doi.org/10.1002/aoc.7402

IF: 3.9

2024-02-29

Applied Organometallic Chemistry

Abstract:A new metal‐organic framework nanocatalyst (Cu@UIO‐66‐AST) has been prepared from UiO‐66‐NH2 through a post‐synthesis modification process. The catalytic efficiency of Cu@UIO‐66‐AST as an acid Lewis was investigated in the synthesis of spiroindole‐pyranopyrazoles. The catalyst can be recycled and reused for up to eight subsequent runs without significant loss of activity. In this work, a new metal–organic framework nanocatalyst (Cu@UIO‐66‐AST) has been prepared from UiO‐66‐NH2 through a post‐synthesis modification process. The Cu (II)@UIO‐66‐AST nanocatalyst formation was confirmed from TGA, FT‐IR, TEM, XRD, BET, CHN, ICP, SEM, EDS, and elemental analyses. The catalytic efficiency of the synthesized MOF (Cu@UIO‐66‐AST), as an acid Lewis, was investigated in the four‐component reaction of isatin, malononitrile, hydrazine, and dimethyl acetylene dicarboxylate and compared to UiO‐66‐NH2 (as a basic catalyst) and Cu (OAc)2 (as an acidic heterogeneous catalyst). The obtained results clearly show that Cu@UIO‐66‐AST has a higher catalytic activity (93%) than UiO‐66‐NH2 (13%) and Cu (OAc)2 (43%). It could be due to the increase of dispersibility of Cu2+ by the formation of several stable complexes between Cu2+ ions and functional groups of ligand AST (OH, C=N, NH, and C‐S) on the surface of the nanocatalyst. Also, the catalyst can be recycled and reused for up to eight subsequent runs without significant loss of activity.

chemistry, inorganic & nuclear, applied