Abstract:Developing hard carbon with a high initial Coulombic efficiency (ICE) and very good cycling stability is of great importance for practical sodium-ion batteries (SIBs). Defects and oxygen-containing groups grown along either the carbon edges or the layers, however, are inevitable in hard carbon and can cause a tremendous density of irreversible Na+ sites, decreasing the efficiency and therefore causing failure of the battery. Thus, eliminating these unexpected defect structures is significant for enhancing the battery performance. Herein, we develop a strategy of applying a soft-carbon coating onto free-standing hard-carbon electrodes, which greatly hinders the formation of defects and oxygen-containing groups on hard carbon. The electrochemical results show that the soft-carbon-coated, free-standing hard-carbon electrodes can achieve an ultrahigh ICE of 94.1% and long cycling performance (99% capacity retention after 100 cycles at a current density of 20 mA g–1), demonstrating their great potential in practical sodium storage systems. The sodium storage mechanism was also investigated by operando Raman spectroscopy. Our sodium storage mechanism extends the "adsorption–intercalation–pore filling–deposition" model. We propose that the pore filling in the plateau area might be divided into two parts: (1) sodium could fill in the pores near the inner wall of the carbon layer; (2) when the sodium in the inner wall pores is close to saturation, the sodium could be further deposited onto the existing sodium.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c12171.Digital picture of the material sandwiched between graphite boards, and SEM image of the carbon paper; digital photograph of large size carbon paper; comparison of XRD, Raman, and infrared spectra of soft carbon; rate performance of HC-P-1200; Nyquist plots of HC-P-1200 and HC-W-1200; full information on operando Raman spectra of the charge–discharge process; periodic variation of the intensity of the charge–discharge for the first cycle, and slope of the second cycle at 1000 and 2000 cm–1 Raman shift (PDF)This article has not yet been cited by other publications.

Introducing the Solvent Co‐Intercalation Mechanism for Hard Carbon with Ultrafast Sodium Storage

Revitalizing Sodium-Ion Batteries Via Controllable Microstructures and Advanced Electrolytes for Hard Carbon

Sodium‐Ion Batteries: Hard–Soft Carbon Composite Anodes with Synergistic Sodium Storage Performance (adv. Funct. Mater. 24/2019)

Consummating ion desolvation in hard carbon anodes for reversible sodium storage

An Overall Understanding of Sodium Storage Behaviors in Hard Carbons by an "Adsorption‐Intercalation/Filling" Hybrid Mechanism

Electrochemical storage mechanism of sodium in carbon materials: A study from soft carbon to hard carbon

High temperature induced abundant closed nanopores for hard carbon as high-performance sodium-ion batteries anodes

From Micropores to Ultra-micropores inside Hard Carbon: Toward Enhanced Capacity in Room-/Low-Temperature Sodium-Ion Storage

Understanding the Sodium Storage Behavior of Closed Pores/Carbonyl Groups in Hard Carbon

Hard Carbon/graphene Microfibers As a Superior Anode Material for Sodium-Ion Batteries

Manipulating Adsorption–Insertion Mechanisms in Nanostructured Carbon Materials for High‐Efficiency Sodium Ion Storage

Hard carbon for sodium storage: Mechanism and performance optimization

Revealing sodium ion storage mechanism in hard carbon

Soft-Carbon-Coated, Free-Standing, Low-Defect, Hard-Carbon Anode To Achieve a 94% Initial Coulombic Efficiency for Sodium-Ion Batteries

Soft-carbon-tuned hard carbon anode for ultrahigh-rate sodium storage

Pore Structure Regulation of Hard Carbon: Towards Fast and High-Capacity Sodium-Ion Storage

Step-by-step desolvation enables high-rate and ultra-stable sodium storage in hard carbon anodes

Preparation of Hard–Soft Carbon Via Co-Carbonization for the Enhanced Plateau Capacity of Sodium-Ion Batteries

Novel Structural Design and Adsorption/Insertion Coordinating Quasi‐Metallic Na Storage Mechanism toward High‐performance Hard Carbon Anode Derived from Carboxymethyl Cellulose

Ultrahigh Plateau‐Capacity Sodium Storage by Plugging Open Pores

The Progress of Hard Carbon as an Anode Material in Sodium-Ion Batteries