Effect of Alloying on Stability of Grain Boundary in Γ Phase of the U–Mo and U–Nb Systems
Zhuoyue Shen,Yi Kong,Yong Du,Shuyuan Zhang
DOI: https://doi.org/10.1016/j.calphad.2020.102241
2021-01-01
Abstract:U-Mo and U-Nb alloys are both extensively used in nuclear industry. gamma phase in U-Mo or U-Nb alloy is a solid solution, being metastable in low temperature region. In this work, the effect of alloying on stability of grain boundary in meta-stable gamma phase in U-Mo and U-Nb alloys are investigate through first-principles calculations. At first, crystal structure and elastic constants of Mo, Nb and gamma-U metals are calculated and the obtain results show the mechanical unstable nature of gamma phase at 0 K, no matter with GGA or GGA + U treatment, which agrees with most of the theoretical results in the literature. Furthermore, from the calculated symmetric tilt grain boundary (STGB) formation energies of Sigma 3[110]/(111) and Sigma 5[001]/(310) in Mo, Nb, and gamma-U, it is found that due to the mechanical unstable character of the gamma-U phase, negative GB formation energy is predicted at 0 K for Sigma 5[001]/ (310) if the STGB model is relaxed with all degrees of freedom. Therefore, by using special quasirandom structure (SQS) method, Sigma 5[001]/(310) and Sigma 3[110]/(111) STGBs with different solute concentrations in U-rich side in U-Mo and U-Nb systems are further investigated. It is found that, when alloying with Mo or Nb, unlike Sigma 3[110]/ (111), although the fixed-atom constraint is applied, the GB formation energy of Sigma 5[001]/(310) STGB is becoming negative when the solute concentration is in U-rich side. Only when the concentration of Mo or Nb is larger than 27 at.% or 30 at.%, respectively, or sufficient small, the GB formation energy is becoming positive, suggesting a cooperative effects of solute concentration, unstable character, and grain size on GB structures in gamma phase. The predicted different stability of alloyed GB structures at 0 K suggest that although gamma phase is metastable at low temperature, its metastability can be controlled through alloying with different solutes, or with different GBs. And grain refinement should be relatively easy in U-rich part than U-poor part of the U-Mo and U-Nb systems.