Abstract:In the present paper, the Al–Fe-Mo phase diagram was studied by X-ray diffraction (XRD), differential thermal analysis, differential scanning calorimetry, scanning electron microscopy and electron probe microanalysis. For the first time, isothermal sections at 1450, 1300 and 1200 °C were experimentally determined over the entire range of compositions. A ternary intermetallic compound τ (Mo 3 FeAl 8 ) with a TiAl 3 -type structure was observed at all above temperatures. It has been shown that isostructural disordered bcc (A2) phases of pure elements Fe and Mo (W-type structure, cI 2 - in the ternary system at 1450 °C form a continuous solid solution (Mo,Fe,Al), dissolving up to 50 at.% Al. When cooled, it decomposes into a Mo-rich part and an elongated area (Fe,Al) along Fe-Al side. As the temperature decreases, their homogeneity regions reduce in size and shift toward higher Mo and Fe contents, respectively. The μ (Mo 6 Fe 7 ) phase, which in the Fe-Mo binary system is formed in the solid state at 1368 °C, deeply extends into the ternary system, up to 16 and 15 at.% at 1300 and 1200 °C, respectively, where Al substitutes for Fe. Since the addition of Mo stabilizes the ε (Fe 5 Al 8 ) phase, and the temperature of its formation in the ternary system is higher than in the binary (1331 and 1234 °C, respectively), the isothermal section at 1300 °C contains a narrow homogeneity region of this phase. In contrast, the solubility of Mo in ε at 1200 °C is no less than 14.4 at.%. The boundary Al-Mo binary and Al–Fe-Mo ternary systems are thermodynamically remodeled based on our experimental results and novel information reported in literature. Thermodynamic modeling was carried out by the CALPHAD (CALculation of PHAse Diagrams) approach using Thermo-Calc software. Calculations performed using the proposed thermodynamic description well reproduce most of the experimental data, including data from the available literature. Based on the developed description, phase diagrams of the constituent binary systems, as well as liquidus and solidus projections, selected isothermal and isopleths sections and the reaction scheme of the ternary system were calculated.

Re-determination of the Pseudobinary System Li2O-MoO3

Phase Equilibria in Quasi-Ternary System Li2O–Mn2O3–Eu2O3

Experimental Investigation and Thermodynamic Modeling of the Li O–Al O System

Thermal Analysis and Phase Diagram of the LiF-BiF3 System

Thermodynamic assessment of the Mo‐Si system

Thermodynamic re-modeling of the binary Al–Mo and ternary Al–Fe–Mo systems based on novel experimental data

Phase Equilibria in the Li–Mn–Eu–O System

Assessment of the thermodynamics and phase diagram of the SrO-B2O3 system

Critical Behavior of Mo-doping La0.67Sr0.33Mn1−xMoxO3 Perovskite System

Re-investigation of the Phase Equilibria and Thermodynamic Assessment of the Mg-Sm Binary System

Phase Behaviors of the Zrmo2-Xwxo8 (X=0.2-2.0) System and the Preparation of an Mo-Rich Cubic Phase

Thermodynamic Calculation of Phase Equilibria in the C-Mo-Zr System

Experimental investigation and thermodynamic modeling of the Mo-Co-B ternary system

Amendment of the Li-Bi Phase Diagram Crystal and Electronic Structure of Li2Bi

Experimental investigation of the phase relations in the SiO2-Dy2O3-CaO ternary system

Solid Solution in Pseudobinary System Ba2YMoO6–

Thermodynamic Modeling of B–Mo–Nb Ternary System with Modified B–Nb Description

Subsolidus Phase Equilibria in the La2O3–(Ni/Со)O–Sb2O5 Systems

Subsolidus phase relationships in the system ZnO–Li2O–WO3

Ternary Reciprocal System Li+, K+ || Br–,

Structure and superconductivity in the binary Re$_{1-x}$Mo$_x$ alloys