Orangish-red light emitting LaSr 2 AlO 5 :Sm 3+ nanophosphors for warm LEDs: Crystallographic, photoluminescence characteristics with high color purity and thermal stability

Pawan Kumar,Devender Singh,Harish Kumar

DOI: https://doi.org/10.1016/j.matchemphys.2024.129418

IF: 4.778

2024-05-04

Materials Chemistry and Physics

Abstract:Gel-combustion method was implemented in current research to generate Strontium Lanthanum Aluminate (LaSr 2 AlO 5 ) phosphors doped with Sm 3+ ions and have a potential to emit orangish-red light. In order to analyze phase characteristics, XRD technique was employed. XRD patterns of synthesized materials were closely resembles the JCPDS pattern indicated on card no. 70-2197, which define the tetragonal symmetry of the material with I4/mcm space group. The morphological, optical band energies and elemental analyses were done via TEM, DRS and EDX investigation respectively. The Sm 3+ activated LaSr 2 AlO 5 phosphor's PL spectra monitored at 406 nm excitation indicate intense visible orangish-red emission at 602 nm owing to the 4 G 5/2 → 6 H 7/2 transition. Concentration quenching was obtained at 4 mol % content of Sm 3+ owed to the dipole-dipole interaction among activated ions. The calculated lifetimes have been observed to shorten as content of Sm 3+ ions in the phosphors rises. The CIE (0.6069, 0.3905) value, CCT (1382 K) value, 99.4 % color purity of the optimum sample was calculated which placed in orange-red space. The fabricated phosphor has excellent thermal durability up to 498 K and 0.1686 eV activation energy. Finally, the results of all the research allow us to consider that Sm 3+ doped LaSr 2 AlO 5 phosphor is appropriate for warm LEDs.

materials science, multidisciplinary