Abstract:Alkaline water electrolysis (AWE) is at a stage of high technological maturity, and modern pressurized designs have mitigated the weaknesses of now-outdated atmospheric electrolyzers. For instance, pressurized systems now deliver high hydrogen outputs and can efficiently adjust to rapid changes in power loads. These improvements were, in part, made possible through significant reductions to internal ohmic losses coming from improved gas separators, shorter distances between electrodes, and increased operating temperatures. From an industrial point of view, the critical parameter to optimize is the full stack voltage. The stack voltage is tightly bound to the individual cell voltage and can thus be lowered by employing more efficient electrocatalysts. However, reducing the cell voltage by raising the temperature of operation—thereby improving both reaction kinetics and the conductivity of the KOH electrolyte—can be of similar or even higher importance (e.g., ca. 4.5 mV/ ̊C, Figure 1) [1]. Therefore, stability under operation at elevated temperatures must be considered when evaluating novel hydrogen and oxygen evolution reaction catalysts for AWE. Else, a novel catalyst risks becoming the bottleneck in the pursuit of higher operating temperatures, limiting its applicability for large-scale electrolysis [2]. Many assessments of novel AWE catalysts are still carried out at room temperature in diluted electrolytes and at low current densities [3]. In the harsher conditions of an electrolyzer, catalysts experience higher dissolution rates and are subject to higher mechanical stress from, for instance, the aggressive bubble evolution. This gap hinders the transfer of catalyst developments from academia to industrial research laboratories and, ultimately, to practical applications. In this work, we attempted to narrow that gap by conducting electrochemical measurements under more application-oriented conditions (i.e., 80-120 °C and 8-11 M KOH). We evaluated the HER activity and the robustness of high-surface-area electrodes produced through controlled leaching of bimetallic nickel-based alloys. A parametric study of the overpotential and robustness as a function of electrochemically active surface area was enabled by varying the synthesis parameters of a Raney-type preparation. Direct coupling to renewable energy sources requires the electrolyzer to frequently and rapidly shut off and on. This intermittent operation induces additional stress on the electrodes as the catalysts transition through different redox states, which is often overlooked in AWE electrocatalyst research. To track redox, compositional, and morphological changes, we used ex situ X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy. At the same time, the dissolution and redeposition of ionic species were monitored using inductively coupled plasma mass spectrometry. By matching the characterization data with the evolution of the overpotential until complete deactivation, we gained an understanding of the degradation mechanisms in high-surface-area nickel-based electrodes. These results shed light on the challenges and prospects of this promising class of electrocatalysts for alkaline HER under industrial conditions. Acknowledgement: This work is partly funded by the Innovation Fund Denmark (IFD) under File No. 1044-00162B. References: [1] Egelund, S. Development of low-cost heterogeneous electrocatalysts for large scale advanced alkaline electrolysers with focus on oxygen evolution and system performance. Ph.D. Dissertation , Technical University of Denmark: Kgs. Lyngby, Denmark, 2015. [2] J. C. Ehlers, A. A. Feidenhans’l, K. T. Therkildsen, and G. O. Larrazábal, “Affordable Green Hydrogen from Alkaline Water Electrolysis: Key Research Needs from an Industrial Perspective,” ACS Energy Lett. 2023 , 8, 3, 1502–1509. [3] McCrory, C. C. L.; Jung, S.; Ferrer, I. M.; Chatman, S. M.; Peters, J. C.; Jaramillo, T. F. Benchmarking Hydrogen Evolving Reaction and Oxygen Evolving Reaction Electrocatalysts for Solar Water Splitting Devices. J. Am. Chem. Soc. 2015 , 137 (13), 4347– 4357. Figure 1

Hydrogen Spillover-Bridged Volmer/Tafel Processes Enabling Ampere-Level Current Density Alkaline Hydrogen Evolution Reaction under Low Overpotential

In Situ Construction of Ni Enriched Porous NiAl As Long-Lived Electrode for Hydrogen Evolution at High Current Densities

Simultaneous Interfacial Chemistry and Inner Helmholtz Plane Regulation for Superior Alkaline Hydrogen Evolution

Hydrogen Spillover Bridged Dual Nano-Islands Triggered by Built-in Electric Field for Efficient and Robust Alkaline Hydrogen Evolution at Ampere-Level Current Density

Enhancing Alkaline Hydrogen Evolution Electrocatalysis Through Hydrogen Spillover in a Ni3S2@Cu2S Heterostructure

Interface Engineering: the Ni(Oh)(2)/Mos2 Heterostructure for Highly Efficient Alkaline Hydrogen Evolution

High current density hydrogen evolution on heterostructured Ni/Cr bimetallic sulfide catalyst in alkaline media

Stabilized Hydroxide Mediated Nickel-Based Electrocatalysts for High Current Density Hydrogen Evolution in Alkaline Media

Unraveling the Synergy of Chemical Hydroxylation and the Physical Heterointerface upon Improving the Hydrogen Evolution Kinetics

Self‐Supported Metallic Alkaline Hydrogen Evolution Electrocatalysts Tolerant for Ampere‐Level Current Densities

Heterogeneous Synergetic Effect of Metal–Oxide Interfaces for Efficient Hydrogen Evolution in Alkaline Solutions

Nanoporous Nonprecious High‐Entropy Alloys as Multisite Electrocatalysts for Ampere‐Level Current‐Density Hydrogen Evolution

Hydrogen Spillover in Pt/Ni(OH)2/Mo2TiC2Tx Electrocatalyst Improves Ph-Universal Hydrogen Evolution Reaction

Synergistic Activation of Crystalline Ni 2 P and Amorphous NiMoO x for Efficient Water Splitting at High Current Densities

Application of Hydrogen Spillover in Alkaline Hydrogen Evolution Reaction

Activity and Stability of High-Surface-Area Nickel-Based Catalysts for the Alkaline Hydrogen Evolution Reaction Under Industrially Relevant Conditions

Design Strategies towards Advanced Hydrogen Evolution Reaction Electrocatalysts at Large Current Densities

Strategies for Designing High-Performance Hydrogen Evolution Reaction Electrocatalysts at Large Current Densities above 1000 mA cm-2

Achieving an efficient hydrogen evolution reaction with a bicontinuous nanoporous PtNiMg alloy of ultralow Noble-metal content at an ultrawide range of current densities

Synergistic Activation of Crystalline Ni2P and Amorphous NiMoO X for Efficient Water Splitting at High Current Densities

A Highly Active and Durable Electrocatalyst for Large Current Density Hydrogen Evolution Reaction.