Comparing the Aging Processes of PLA and PE: The Impact of UV Irradiation and Water

Xucheng Wang,Jinxin Chen,Wenhao Jia,Kaibo Huang,Yini Ma

DOI: https://doi.org/10.3390/pr12040635

IF: 3.5

2024-03-23

Processes

Abstract:The aging processes of microplastics (MPs) are prevalent in natural environments. Understanding the aging mechanisms of MPs is crucial for assessing their environmental behavior and potential risks. In this study, we selected polylactic acid (PLA) and polyethylene (PE) as representatives of biodegradable and conventional plastics, respectively, to examine changes in their physicochemical properties induced by water and UV light exposure. Laboratory aging resulted in significant fragmentation, characterized by cracks and pores on the surfaces, for both types of MPs, with PLA MPs exhibiting more severe changes, particularly under combined UV and water exposure. Notably, PLA MPs tended to become progressively smaller after aging, whereas PE MPs did not show significant size changes. Chemical analyses of aged MPs using micro-Fourier-transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS) revealed a substantial increase in the carbonyl index (CI) and oxygen content for PE, suggesting surface oxidation during photo-oxidation. Conversely, PLA MPs displayed a CI decrease, along with an oxygen content increase, indicating the breakdown of ester linkages in PLA and the formation of other oxidation products. Furthermore, we developed and optimized pyrolysis–gas chromatography–mass spectrometry (Py–GC–MS) methods to identify potential chemical degradation products of PE and PLA, considering their differing thermal stabilities. We observed a distinct trend regarding the peaks in the chromatogram of aged MPs and identified the typical oxidation and crosslinking products for PLA. Additionally, after the aging process, both PE and PLA exhibited a significant increase in organic carbon content, with the eluate containing submicron/nano-sized particles. This study provides a scientific foundation for a deeper understanding of the environmental aging mechanisms of various MPs, particularly in regards to the effects of UV irradiation and water exposure.

engineering, chemical

What problem does this paper attempt to address?

The problems that this paper attempts to solve are:

The aging process of microplastics (MPs) in the natural environment and their impact on environmental behavior and potential risks. Specifically, the study selected polylactic acid (PLA) and polyethylene (PE) as representatives of biodegradable plastics and traditional plastics respectively, and explored the changes in their physicochemical properties under water and ultraviolet (UV) irradiation. The study focuses on the following aspects:

1. **Photodegradation and hydrolysis mechanisms**: The study aims to explore the photodegradation and hydrolysis mechanisms of PE and PLA in water and air environments.
2. **Particle size changes**: The study analyzed the changes in particle size of PE and PLA plastics during the aging process under UV irradiation, as well as the relationship between the process of generating smaller - sized micro - and nano - plastic particles and dissolved organic matter.

Through these studies, the author hopes to provide a scientific basis for the degradation patterns and environmental behaviors of two typical plastic polymers.