Effect of graphene oxide on tensile and flexural properties of carbon/glass hybrid fiber‐reinforced polymer composite
Hongwei Zhang,Xiaoping Gao,Hongxia Li,Wei Wu,Shiyuan Sun
DOI: https://doi.org/10.1002/pc.26228
IF: 5.2
2021-08-16
Polymer Composites
Abstract:In this article, we used the biaxial warp-knitted carbon/glass hybrid fibers as the reinforcement, the epoxy resin as the matrix, and the vacuum-assisted resin transfer-molding technique to prepare composite materials modified with different mass fractions of graphene oxide (GO) to investigate the influence of GO on the mechanical properties of carbon/glass hybrid fiber reinforced composites. The tensile and bending properties of the samples along the 0° and 90° directions were tested experimentally, and the macro- and micro-morphology characteristics of the fractured specimens were observed. The influence of GO modification on the strength and modulus of the composite material was analyzed. The results showed that GO modification improves the bonding strength of fiber/resin interface, tensile, and bending properties. Notably, when the filling content was 0.25 wt%, the tensile strength along the 0° and 90° directions increased by 8.97 and 4.78%, respectively. Similarly, the tensile modulus increased by 15.19 and 10.74%, respectively. Besides, the bending strength along the 0° and 90° directions increased by 10.70 and 9.60%, respectively, whereas the bending modulus increased by 9.62 and 15.20%, respectively. Therefore, the GO-modified carbon/glass hybrid fiber-reinforced composite materials exhibit improved mechanical properties, hence can be applied in wide range of applications.
materials science, composites,polymer science