Lanthanide-doped NaYF 4 near-infrared-II nanothermometers for deep tissue temperature sensing
Xiangyang Yuan,Endian Cui,Kai Liu,Ying Jiang,Xiaoyan Yang,Jianfeng Tang,Lu Yang,Xiaoling Liao,Yanan Zhao,Wei Sun,Yingshuai Liu,Jing Liu
DOI: https://doi.org/10.1016/j.ceramint.2022.08.110
IF: 5.532
2022-11-08
Ceramics International
Abstract:In this work, different lanthanides (Tm 3+ , Er 3+ ; Yb 3+ , Ho 3+ , Nd 3+ ) were doped into NaYF 4 via a high-temperature coprecipitation method, and followed by SiO 2 coating to improve the water dispersibility, resulting in NaYF 4 :Tm 3+ , Er 3+ @NaYF 4 @SiO 2 and NaYF 4 :Yb 3+ , Ho 3+ @NaYF 4 :Nd 3+ @SiO 2 nanoparticles (NPs). The two NPs both exhibited the temperature-dependent second near-infrared (NIR-II) downshifting luminescence over the physiological range. The luminescence ratio of Tm 3+ emission at 1460 nm to Er 3+ emission at 1525 nm (Tm 3+ : 3 H 4 → 3 F 4 ; Er 3+ : 4 I 13/2 → 4 I 13/2 ) varies with temperature increase, as well as Yb 3+ emission at 980 nm and Ho 3+ emission at 1150 nm (Yb 3+ : 2 F 5/2 → 2 F 7/2 ; Ho 3+ : 5 I 6 → 5 I 8 ). The highest relative sensitivity of NaYF 4 :Tm 3+ , Er 3+ @NaYF 4 @SiO 2 and NaYF 4 :Yb 3+ , Ho 3+ @NaYF 4 :Nd 3+ @SiO 2 aqueous suspension is 0.36% K −1 (at 298 K) and 0.76% K −1 (at 343 K), respectively. The biological tests prove the good biocompatibility and low toxicity of the water-soluble NPs. In vitro tissue penetration experiments verify a much better penetration ability of the synthesized NaYF 4 :Tm 3+ , Er 3+ @NaYF 4 @SiO 2 compared with NaYF 4 :Yb 3+ , Ho 3+ @NaYF 4 :Nd 3+ @SiO 2 NPs. The excellent physiological luminescent thermometry with favor wave penetration depth provides a promising platform in deep tissue temperature measurement, which is very important in vivo biosensing.
materials science, ceramics