Hole-Transport-Underlayer-Induced Crystallization Management of Two-Dimensional Perovskites for High-Performance Inverted Solar Cells

Zhihai Liu,Lei Wang,Chongyang Xu,Xiaoyin Xie,Yuhai Zhang

DOI: https://doi.org/10.1021/acsaem.1c01531

IF: 6.4

2021-09-24

ACS Applied Energy Materials

Abstract:Currently, intensive research is being conducted on Ruddlesden–Popper-type two-dimensional (2D) perovskite-based solar cells because of the advantages such as excellent power conversion efficiency (PCE) and desirable environmental stability. A well-crystallized perovskite film plays a very important role in enhancing the performance of perovskite solar cells (PSCs). In this study, we investigated the effect of the wetting property of the underlying hole-transport layer (HTL) on the crystallization of 2D perovskite films. Three HTL layers with varied hydrophobicities, including hydrophilic poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS), moderate-hydrophobic poly(bis(4-phenyl)(2,4,6-trimethylphenyl)amine) (PTAA), and high-hydrophobic poly(3-hexylthiophene-2,5-diyl) (P3HT), were used to fabricate 2D PSCs, and the quality of the resulting perovskite films was examined. We found that moderate-hydrophobic PTAA resulted in a compact and uniform perovskite morphology with enhanced crystallinity. By contrast, the perovskite film formed on hydrophilic PEDOT:PSS showed a rough morphology with overlapping perovskite planes. This is because the hydrophobic PTAA surface could suppress the heterogeneous nucleation of perovskite and facilitate the boundary mobility of perovskite grains. Therefore, a high PCE value of 12.3% was achieved for the PTAA-based PSCs, which is higher than that of the PSCs using PEDOT:PSS (10.5%). However, the perovskite film formed on the highly hydrophobic P3HT showed a low surface coverage, resulting in an even lower PCE of 8.3%. This might be due to the higher hydrophobicity of P3HT, which leads to a low adhesion force with the precursor. The 2D PSCs using PTAA also show better long-term and thermal stability than the PEDOT:PSS-based case, with a suppressed PCE degradation from 26 to 17%. Our results indicate that using moderate-hydrophobic PTAA as the HTL is beneficial for fabricating efficient 2D PSCs with higher stability.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c01531.Contact angle of pristine PTAA (Figure S1), J–V characteristics of P3HT-based PSCs (Figure S2), UV–vis absorption spectrum of the P3HT film (Figure S3), J–V characteristics and device parameters of PTA-based PSCs (Figure S4 and Table S1), transmission spectra of PEDOT:PSS and PTAA films (Figure S5), dark J–V characteristics of the PSCs (Figure S6), and stability measurements (Figure S7) (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical,energy & fuels