Efficiency and sustainable leaching process of manganese from pyrolusite-pyrite mixture in sulfuric acid systems enhanced by microwave heating

Shunda Lin,Lei Gao,Yong Yang,Jin Chen,Shenghui Guo,Mamdouh Omran,Guo Chen
DOI: https://doi.org/10.1016/j.hydromet.2020.105519
IF: 4.217
2020-12-01
Hydrometallurgy
Abstract:<p>Recently, with the decrease in the quality of manganese resources, the efficient use of low-quality manganese ore resources has attracted widespread attention. At present, pyrite is often used as reducing agent to recover Mn(IV) in industrialization. However, the passivation of pyrite in the leaching reaction process will lead to a decreased reaction efficiency. Hence, in this study, microwave heating was applied in the reduction system in order to remove the inhibition of the passivation layer and accelerate the dissolution of pyrite, indicating an improvement in the corresponding Mn(IV) reduction efficiency. The results show that the leaching rate assisted by microwave heating was 95.07%, approximately 20% higher than that of conventional heating (75.08%), and the amount of sulfuric acid and pyrite was reduced by 14% and 20%, respectively. XPS analysis shows that there was an obvious sulfur elemental peak at 164.3 eV under traditional heating conditions, but it was absent when microwave heating was applied, and the elemental sulfur under conventional heating is 11.63%, which is higher than that under microwave heating (4.80%). Through scanning electron microscopy, it was noted that there are a large number of voids on the mineral surface under microwave heating, which can increase the solid-liquid contact area, effectively reducing the formation of the sulfur passivation layer and accelerating the dissolution of Mn (IV). In addition, the measurement of the dielectric constant of the solution mixture shows that the dielectric constant of the solution with mineral addition was increased from 36.533 (F/M) to 37.717 (F/M) and the loss tangent angle was increased from 8.61 × 10<sup>−3</sup> to 9.21 × 10<sup>−3</sup>. It can be inferred that microwaves act directly on the mineral itself through the solution. Thus, the application of pyrite and microwave heating in the recovery of Mn(IV) is expected to effectively reduce the use of sulfuric acid, and achieve green, environmentally friendly and efficient leaching of manganese.</p>
metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to improve the efficiency and sustainability of manganese leaching from low - grade pyrolusite - pyrite mixtures. Specifically, the researchers improve the reductive leaching process in the traditional sulfuric acid system by introducing microwave heating technology. This method aims to overcome the problem of decreased reaction efficiency caused by the formation of a passivation layer on the pyrite surface during the traditional heating process, thereby increasing the reduction efficiency of Mn(IV) and reducing the amounts of sulfuric acid and pyrite used, achieving more environmentally - friendly and efficient manganese resource recovery. ### Background and Problem of the Paper With the decline in the quality of manganese resources, the efficient utilization of low - grade manganese ore resources has become increasingly important. Currently, pyrite is commonly used as a reducing agent in industry to recover Mn(IV), but pyrite is prone to form a passivation layer during the leaching reaction process, resulting in a reduced reaction efficiency. Therefore, the researchers attempt to apply microwave heating technology in the reduction system to remove the influence of the passivation layer, accelerate the dissolution of pyrite, and improve the reduction efficiency of Mn(IV). ### Main Research Contents 1. **Effect of Microwave Heating on Leaching Efficiency**: - The research found that with the assistance of microwave heating, the leaching rate reached 95.07%, which was approximately 20% higher than that of traditional heating (75.08%). - Microwave heating also reduced the amounts of sulfuric acid and pyrite used, by 14% and 20% respectively. 2. **Formation and Elimination of the Passivation Layer**: - XPS analysis showed that under traditional heating conditions, the sulfur element peak appeared at 164.3 eV, while this peak disappeared under microwave heating, indicating that microwave heating effectively reduced the formation of the sulfur passivation layer. - Observation by scanning electron microscope (SEM) showed that a large number of pores were formed on the mineral surface under microwave heating, increasing the solid - liquid contact area, effectively reducing the formation of the sulfur passivation layer and accelerating the dissolution of Mn(IV). 3. **Change in Dielectric Constant of the Solution**: - Measurement results showed that after adding minerals, the dielectric constant of the solution increased from 36.533 (F/M) to 37.717 (F/M), and the loss tangent increased from 8.61 × 10⁻³ to 9.21 × 10⁻³. - This indicates that the microwave directly acts on the mineral itself and transfers energy through the solution, improving the reaction efficiency. ### Conclusion Through the application of microwave heating technology, the leaching efficiency of manganese in low - grade pyrolusite can be significantly improved, the amounts of sulfuric acid and pyrite used can be reduced, and green, environmentally - friendly and efficient manganese resource recovery can be achieved. This method provides new ideas and technical support for the comprehensive utilization of low - grade manganese ore resources.