Engineering In‐Plane Nickel Phosphide Heterointerfaces with Interfacial sp HP Hybridization for Highly Efficient and Durable Hydrogen Evolution at 2 A cm −2
Qian Zhou,Liling Liao,Qihang Bian,Fang Yu,Dongyang Li,Jinsong Zeng,Long Zhang,Hui Wang,Dongsheng Tang,Haiqing Zhou,Zhifeng Ren
DOI: https://doi.org/10.1002/smll.202105642
IF: 13.3
2021-11-25
Small
Abstract:The catalytic hydrogen-evolving activities of transition-metal phosphides are greatly related to the phosphorus content, but the physical origin of performance enhancement remains ambiguous, and tuning the catalytic activity of nickel phosphides (NiP<sub>2</sub> /Ni<sub>5</sub> P<sub>4</sub> ) remains challenging due to unfavorable H* adsorption. Here, a strategy is introduced to integrate P-rich NiP<sub>2</sub> and P-poor Ni<sub>5</sub> P<sub>4</sub> into in-plane heterostructures by anion substitution, in which P atoms at the in-plane interfaces perform as active sites to adsorb H* and thus facilitate the hydrogen evolution reaction (HER) process via modulating the electronic structure between NiP<sub>2</sub> and Ni<sub>5</sub> P<sub>4</sub> . Consequently, the NiP<sub>2</sub> /Ni<sub>5</sub> P<sub>4</sub> hybrid exhibits an outstanding hydrogen-evolving activity, requiring only 30 and 76 mV to afford 10 and 100 mA cm<sup>-2</sup> in acid, respectively. It surpasses most of the earth-abundant electrocatalysts thus far, and is comparable to Pt catalysts (30/72 mV at 10/100 mA cm<sup>-2</sup> ). Particularly, it can run smoothly at large current density and only requires 247 mV to reach 2000 mA cm<sup>-2</sup> . Detailed theoretical calculations reveal that its exceptional activity stems from the moderate overlap of density states between P 2p and H 1s orbitals, thus optimizing the H*-adsorption strength. This work highlights a new avenue toward the fabrication of robust non-noble electrocatalysts by constructing in-plane heterojunctions.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology