Multifunction-balanced porous carbon and its application in sulfur-loading host and separator modification for lithium–sulfur batteries
Shengheng Nong,Dongyuan Huang,Yaoying Li,Ruoxi Yang,Jiawei Xie,Jia Li,Haifu Huang,Xianqing Liang,Guangxu Li,Zhiqiang Lan,Haizhen Liu,Dan Huang,Shuaikai Xu,Jin Guo,Wenzheng Zhou
DOI: https://doi.org/10.1016/j.est.2023.110296
IF: 9.4
2024-01-13
Journal of Energy Storage
Abstract:Lithium–sulfur batteries have been researched extensively because of their high energy density and low price. However, the poor conductivity of sulfur, the shuttle effect of polysulfide , the slow redox kinetics of sulfur species, and the significant volume expansion and contraction during charging and discharging have hindered the commercial application of lithium–sulfur batteries. In this study, a simple, scalable, and cost-effective strategy was developed to control the balance of the porosity, specific surface area, graphitization, heteroatom co-doping, and polar-polar interactions of a biomass carbon source. With this strategy, multifunctional porous carbon materials with three-dimensional network structures were prepared to serve as sulfur-loading hosts with high specific surface area, strong adsorption activity, and good conductivity. Moreover, the optimal porous carbon material was directly coated on a commercial separator, and the modified separator was found to further improve the electrochemical performance of a lithium–sulfur battery. As a result, for the battery with GPCS-3 as cathode electrode and modified separator as separator, the initial discharge capacity at 1.0C is 926.2 mAh g −1 . After 300 cycles, the discharge capacity is 712.7 mAh g −1 , and the average capacity decay is only 0.077 % per cycle. Since the three-dimensional network structure material exhibits good performance as a sulfur-loading host as well as the ability to effectively modify a separator, this study provides a valuable strategy for the fabrication of high energy density lithium–sulfur batteries.
energy & fuels