Abstract:Graded lattice structures (GLSs) have drawn much attention in engineering and biological areas due to the enhanced mechanical properties and energy absorption capacity that benefit from the graded design. This study aims to investigate the effect of gradient on fatigue behaviors of lattice structures under the cyclic loading lateral to the gradient direction. The Gyroid-type triply periodic minimal surface was utilized to design GLS with continuously varied volume fraction (VF) from 10% to 40%. Uniaxial compressive testing and compression-compression fatigue testing were conducted on the Ti-6Al-4V Gyroid lattice structures with both uniform and graded VFs fabricated by laser powder bed fusion. Three typical fracture modes and mixed fracture modes were all observed on the fracture surfaces of struts after fatigue testing. The fatigue life of Gyroid GLSs is 1.21–1.67 times that of uniform counterparts with an identical overall VF. The enhancement mechanism on fatigue properties coming from the gradient design is elaborated through the finite element analysis and experimental characterization. The lower level of tensile stress, bigger macro-area and micro-plastic zone on struts of the main loading-bearing constituent of Gyroid GLS relieve the stress concentration around the crack tip, thus, lower the crack propagation rate and provide stronger fatigue crack resistance. Furthermore, the struts in the main loading-bearing constituent are more prone to stretching, therefore, provide long-term carrying capacity even after the occurrence of penetrating cracks. Experiment results show that the carrying capacity can be still provided by these struts even with penetrating cracks.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the influence of gradient design on the fatigue properties of Ti - 6Al - 4V Gyroid graded lattice structures (GLSs) manufactured by laser powder bed fusion (L - PBF). Specifically, the researchers are concerned with how gradient design affects the fatigue behavior of these materials under cyclic loading, especially when the loading direction is perpendicular to the gradient direction. Through this study, the author hopes to reveal how gradient design improves the fatigue life of these materials and explore the underlying strengthening mechanisms. The key points mentioned in the paper include: 1. **Research Background**: Graded lattice structures have received extensive attention in the engineering and biological fields due to their enhanced mechanical properties and energy absorption capabilities. However, relatively few studies have been conducted on the fatigue properties of these structures, especially regarding the negative impacts of internal defects and adhered powder on fatigue properties during the L - PBF manufacturing process. 2. **Research Purpose**: This study aims to explore the influence of gradient design on the fatigue properties of Ti - 6Al - 4V Gyroid graded lattice structures through experiments and finite - element analysis, especially when the loading direction is perpendicular to the gradient direction. 3. **Research Methods**: - **Design and Manufacture**: Gyroid graded lattice structures with continuously varying volume fractions (VF) from 10% to 40% were manufactured using L - PBF technology, as well as uniform lattice structures with the same overall VF. - **Testing Methods**: Quasi - static compression tests and compression - compression fatigue tests were carried out to evaluate the mechanical properties and fatigue life of these structures. 4. **Research Results**: - **Fatigue Life**: The results show that the fatigue life of Gyroid graded lattice structures is 1.21 to 1.67 times higher than that of uniform lattice structures with the same overall VF. - **Strengthening Mechanisms**: Through finite - element analysis and experimental characterization, it was found that gradient design reduces the tensile stress level, increases the macroscopic area and micro - plastic region, alleviates the stress concentration at the crack tip, thereby reducing the crack growth rate and providing stronger fatigue crack resistance. - **Micro - mechanisms**: The struts in the main load - bearing parts are more likely to elongate after fatigue testing and can provide long - term load - bearing capacity even if through - cracks occur. 5. **Conclusion**: Gradient design significantly improves the fatigue properties of Ti - 6Al - 4V Gyroid lattice structures, which provides important theoretical support and technical guidance for these materials in applications requiring long - term service.

Fatigue properties of Ti-6Al-4V Gyroid graded lattice structures fabricated by laser powder bed fusion with lateral loading

Quasi-Static compressive responses and fatigue behaviour of Ti-6Al-4 V graded lattice structures fabricated by laser powder bed fusion

Effect of the direction of the gradient on the mechanical properties and energy absorption of additive manufactured Ti-6Al-4 V functionally graded lattice structures

Mechanical Properties Evaluation Based on the Variable Gradient of Body-Centered-Cubic-Based Lattice Structure Prepared by Laser Powder Bed Fusion

Ni–Ti multicell interlacing Gyroid lattice structures with ultra-high hyperelastic response fabricated by laser powder bed fusion

Compressive properties of Ti6Al4V Functionally Graded Lattice Structures via topology optimization design and selective laser melting fabrication

Network-Based Radial-Gradient Al–Si10–Mg Gyroid Lattice Structures: Manufacture, Mechanical Response and Energy Absorption

Mechanical properties of three-dimensional functionally graded TPMS structures

Effects of porosity gradient pattern on mechanical performance of additive manufactured Ti-6Al-4V functionally graded porous structure

The effect of microstructure on the fatigue behavior of titanium alloy graded porous structures fabricated by selective laser melting

Mechanical responses of sheet-based gyroid-type triply periodic minimal surface lattice structures fabricated using selective laser melting

Investigation of Compressive Properties of Graded Lattice Structure with Different Porosity Gradient Spans Prepared by Selective Laser Melting

Finite element analysis of the mechanical properties of sheet- and skeleton-gyroid Ti6Al4V structures produced by laser powder bed fusion

Design and mechanical performances of a novel functionally graded sheet-based lattice structure

Mechanical behavior and failure mode of body-centered cubic, gyroid, diamond, and Voronoi functionally graded additively manufactured biomedical lattice structures

Optimisation of Selective Laser Melted Ti6Al4V Functionally Graded Lattice Structures Accounting for Structural Safety

Investigation of fatigue behavior of laser powder bed fusion Ti-6Al-4V: Roles of heat treatment and microstructure

Evaluating quasi-static and fatigue performance of IN718 gyroid lattice structures fabricated via LPBF: Exploring relative densities

Mechanical Response of Gradient Lattice Structures Based on Topology Optimization

Enhancing specific energy absorption of additively manufactured titanium lattice structures through simultaneous manipulation of architecture and constituent material

Evaluation of mechanical properties of Ti–6Al–4V BCC lattice structure with different density gradient variations prepared by L-PBF