Structural, optical, magnetic and dielectric studies of SnO2 nano particles in real time applications

V. Siva Jahnavi,Sumanta Kumar Tripathy,A.V.N. Ramalingeswara Rao

DOI: https://doi.org/10.1016/j.physb.2019.04.020

2019-07-01

Abstract:<p>Pure and Aluminium doped (x = 0.01, 0.02, 0.03, 0.04) SnO₂ nano particles have been prepared by Sol Gel method. XRD studies confirm tetragonal structure of SnO₂ and second phase peaks are absent. The obtained crystallite size of undoped SnO₂ is 17.5 nm and with Al insertion Crystallite size reduced to 10 nm for Sn_0.96Al_0.04O₂. FTIR data in the range of 550 cm⁻¹–630 cm⁻¹ confirms the vibration modes of SnOSn and SnO in SnO₂ molecules. UV spectrum shows red shift due to the trapping of exitons by oxygen vacancies. In contrast to quantum confinement energy gap decreases from 3.7 eV for undoped SnO₂ and to 2.91 eV for Sn_0.97Al_0.03O₂ due to the band bending, which is the result of particle size reduction and then increases to 3.19 eV. This variation has been explained based on Burstein-Moss effect for Sn_0.96Al_0.04O₂. Impedance studies of undoped and Al doped SnO₂ samples have been investigated at room temperature and found that Sn_0.97Al_0.03O₂ exhibits peculiar behaviour of having high dielectric constant, high A.C. conductivity, low dielectric loss and high theoretically calculated mobility among Al doped SnO₂ samples. The data obtained from Vibration Sample Magnetometer shows typical conversion of magnetic nature of undoped SnO₂ which is diamagnetic to paramagnetic in the case of Sn_0.99Al_0.01O_{2 and} Sn_0.98Al_0.02O₂ samples and to superparamagnetic nature for Sn_0.97Al_0.03O₂ and Sn_0.96Al_0.04O₂.</p>