Shankee Verma,Bisweswar Santra,Arunkumar S,Subbiah Alwarappan,Y S Katharria,Aloke Kanjilal

DOI: https://doi.org/10.1088/1402-4896/ad837c

2024-10-05

Physica Scripta

Abstract:Tuning the optical properties of graphene oxide (GO) by making composites with 2D materials has attracted considerable interest for various applications. Here, the g-C 3 N 4 @GO composite is synthesised by a two-step modified Hummer's method with 3 wt.% and 7 wt.% g-C 3 N 4 . Structural and chemical properties of GO and with g-C 3 N 4 are investigated by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), respectively, while scanning electron microscopy reveals a flake-like structure in g-g-C 3 N 4 @GO composites. Raman analysis gives an increase in I D /I G ratio from 3.1 to 3.2 due to the formation of defects for 3 wt.% g-C 3 N 4 but reduced to 2.9 with 7 wt.% g-C 3 N 4 . Optical bandgap of GO (~3.35 eV) is reduced to ~3.30 eV (3 wt.% g-C 3 N 4 ) and ~3.25 eV (7 wt.% g-C 3 N 4 ) with respective defect edges at ~2.53 eV, 2.52 eV and 2.50 eV, in good agreement with the photoluminescence (PL) results. The appearance of a broad XRD peak at ~23.2o signifies the formation of rGO by reducing GO with g-C 3 N 4 , where the existence of HO-C=O in XPS analysis reveals the formation of defects. This is found to be associated with a chemical reaction at the g-C 3 N 4 /GO interfaces and thus makes this system promising with increased PL intensity.

physics, multidisciplinary