Self‐Assembled Perovskite Nanowire Clusters for High Luminance Red Light‐Emitting Diodes

Chenghao Bi,Jingcong Hu,Zhiwei Yao,Yue Lu,David Binks,Manling Sui,Jianjun Tian

DOI: https://doi.org/10.1002/adfm.202005990

IF: 19

2020-09-15

Advanced Functional Materials

Abstract:<p>Bright red emission (620–650 nm) from perovskite light‐emitting diodes (PeLEDs) is usually achieved via a composition including both bromine and iodine anions, which results in poor performance and stability due to phase separation under operating conditions. Here a large‐scale ligand‐assisted reprecipitation method is devised with nonpolar solvent that enables the fabrication of CsPbI₃ nanowire clusters, emitting at 600 nm. The blue‐shift of this emission relative to that of bulk CsPbI₃ (≈700 nm) is attributed to quantum confinement in nanowires. The growth of the nanowires is along the [011] crystal direction and is vacancy driven, resulting in the healing of surface defects and thereby a high photoluminescence quantum yield of 91%. The clusters with ultralow trap density show remarkable structural and environmental stability. PeLEDs based on these clusters exhibit an external quantum efficiency of 6.2% with Commission Internationale de l'Eclairage coordinates of (0.66, 0.34), and record luminance of 13 644 cd m⁻² of red electroluminescence. The half‐lifetime under an accelerated stability test is 13.5 min for an unencapsulated device in ambient conditions operating at an initial luminance of 11 500 cd m⁻², which corresponds to an estimated half‐lifetime of 694 h at 100 cd m⁻² based on acceleration factor obtained by experimental testing.</p>

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the performance and stability issues when perovskite materials are used in red - light - emitting diodes (PeLEDs). Specifically, traditional red perovskite light - emitting diodes (with an emission wavelength between 620 - 650 nm) are usually achieved through perovskite compositions containing bromine and iodine anions. However, this mixed - halide perovskite is prone to phase separation under operating conditions, resulting in structural instability and poor performance. In addition, the mixing of halogens will lead to rapid ion migration and high non - radiative losses, further affecting the performance and stability of the device.

To overcome these problems, the authors proposed a new method, that is, by using a large - scale ligand - assisted reprecipitation method (LARP) to prepare CsPbI₃ nanowire clusters with non - polar solvents. This method can achieve a blue - shift emission at 600 nm, which is due to the quantum confinement effect. These nanowire clusters have an ultra - low trap density and show remarkable structural and environmental stability. PeLEDs based on these nanowire clusters exhibit an external quantum efficiency (EQE) of 6.2%, CIE coordinates of (0.66, 0.34) and a record - breaking brightness of 13,644 cd m⁻², and these performance indicators are very excellent for red - light PeLEDs.

In addition, this study also evaluated the long - term operational stability of these PeLEDs. In the case of being unpackaged, the half - life is 13.5 minutes at an initial brightness of 11,500 cd m⁻². According to the acceleration factor calculation, at an initial brightness of 100 cd m⁻², the estimated half - life is 694 hours, which indicates the potential value of these devices in practical applications. In conclusion, this study aims to improve the performance and stability of red - light PeLEDs by developing new perovskite nanomaterials, thereby promoting their application in high - resolution display technologies.