Micro-meso porous structured carbon nanofibers with ultra-high surface area and large supercapacitor electrode capacitance

He Wang,Haitao Niu,Hongjie Wang,Wenyu Wang,Xin Jin,Hongxia Wang,Hua Zhou,Tong Lin

DOI: https://doi.org/10.1016/j.jpowsour.2020.228986

IF: 9.2

2021-01-01

Journal of Power Sources

Abstract:<p>Carbon nanofibers from electrospun polymer nanofibers have received considerable attention. However, most of the carbon nanofibers with a surface area above 1000 m²/g were reported to have a supercapacitor electrode capacitance far below 350 F g⁻¹. Herein, we report a novel carbon nanofibrous material that has a supercapacitor electrode capacitance as high as 394 F g⁻¹ (1.0 A g⁻¹). We used a polymer blend of polyacrylonitrile (PAN) and novolac (NOC) as materials, to electrospin them into precursor nanofibers and subsequently carbonize the nanofibers into carbon nanofibers. The carbon nanofibers prepared had a specific surface area as high as 1468 m² g⁻¹ with a meso-micro pores (average pore size 2.2 nm) predominated porous structure. The carbon nanofiber electrodes after 10,000 cycles of charging and discharging at 1.0 A g⁻¹ maintained the capacitance almost unchanged. At the optimal condition, the supercapacitor device made of the electrodes had an energy density as high as 13.6 Wh∙kg⁻¹ (at 0.5 kW kg⁻¹). The high capacitance value comes from the carbon nanofibers with a large surface area and a unique porous structure. The high inter-fiber interconnection contributes to high capacitance. This super-high surface area carbon may be useful for the development of high-performance supercapacitors and other energy devices.</p>

energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical

What problem does this paper attempt to address?

The paper attempts to address the issue of simultaneously achieving high specific surface area and high capacitance values in supercapacitor electrode materials. Specifically, most reported carbon nanofibers with a specific surface area exceeding 1000 m²/g have supercapacitor electrode capacitance values far below 350 F/g. This paper aims to develop a novel carbon nanofiber material that not only possesses an ultra-high specific surface area (up to 1468 m²/g) but also significantly improves the capacitance value of supercapacitor electrodes, reaching 394 F/g (at a current density of 1.0 A/g). Additionally, this material can maintain an almost unchanged capacitance value after 10,000 charge-discharge cycles, and under optimal conditions, the energy density of supercapacitor devices made from this material can reach up to 13.6 Wh/kg (at a power density of 0.5 kW/kg).

To achieve this goal, the researchers used a blend of polyacrylonitrile (PAN) and phenolic resin (NOC) as the precursor. They prepared precursor nanofibers through electrospinning technology, followed by carbonization treatment to obtain carbon nanofibers with a microporous-mesoporous structure. Experimental results indicate that this unique structure and high specific surface area are key factors in achieving high capacitance values.