Abstract:Bobbin tool friction stir welding (BT-FSW) is characterized by a fully penetrated pin and double-sided shoulder that promote symmetrical solid-state joints. However, control of the processing parameters to obtain defect-free thick lap joints is still difficult and needs more effort. In this study, the BT-FSW process was used to produce 10 mm AA1050-H14 similar lap joints. A newly designed bobbin tool (BT) with three different pin geometries (cylindrical, square, and triangular) and concave shoulders profile was designed, manufactured, and applied to produce the Al alloy lap joints. The experiments were carried out at a constant tool rotation speed of 600 rpm and a wide range of various welding travel speeds of 200, 400, 600, 800, and 1000 mm/min. The generated temperature during the BT-FSW process was recorded and analyzed at the joints' center line, and at both advancing and retreating sides. Visual inspection, macrostructures, hardness, and tensile properties were investigated. The fracture surfaces after tensile testing were also examined. The results showed that the pin geometry and travel speed are considered the most important controlling parameters in BT-FSW thick lap joints. The square (Sq) pin geometry gives the highest BT-FSW stir zone temperature compared to the other two pins, cylindrical (Cy) and triangular (Tr), whereas the Tr pin gives the lowest stir zone temperature at all applied travel speeds from 200 to 1000 mm/min. Furthermore, the temperature along the lap joints decreased with increasing the welding speed, and the maximum temperature of 380 °C was obtained at the lowest travel speed of 200 mm/min with applying Sq pin geometry. The temperature at the advancing side (AS) was higher than that at the retreating side (RS) by around 20 °C. Defect-free welds were produced using a bobbin tool with Cy and Sq pin geometries at all the travel welding speeds investigated. BT-FSW at a travel speed of 200 mm/min leads to the highest tensile shear properties, in the case of using the Sq pin. The hardness profiles showed a significant effect for both the tool pin geometry and the welding speed, whereas the width of the softened region is reduced dramatically with increasing the welding speed and using the triangular pin.

Influence of Bobbin Tool on Microstructure, Residual Stress, Tool and Corrosion Analysis of Al 6063 Alloy Friction Stir Welded Joint

Microstructural Characterization of Friction Stir Welds of Aluminum 6082 Produced with Bobbin Tool

Bobbin Tool Friction Stir Welding of Aluminum Thick Lap Joints: Effect of Process Parameters on Temperature Distribution and Joints' Properties

Studies on Effect of Tool Pin Profiles and Welding Parameters on the Friction Stir Welding of Dissimilar Aluminium Alloys AA5052 & AA6063

Microstructure and Mechanical Properties Analysis of Al/Cu Dissimilar Alloys Joining by Using Conventional and Bobbin Tool Friction Stir Welding

Mechanical properties, microstructure, and fracture behavior of friction stir welded AA7075 joints with conical pin and conical threaded pin type tools

The Influence of Tool Geometry on the Mechanical Properties and the Microstructure of AA6061-T6 Aluminum Alloy Friction Stir Spot Welding

Effects of friction stir welding on corrosion and mechanical properties of AA6063 in sea water

The Influence of Tool Shape and Process Parameters on the Mechanical Properties of AW-3004 Aluminium Alloy Friction Stir Welded Joints

Welding Investigation on AA6063-T6 Aluminium alloy during Friction Stir Welding process

Effect of Tool Profile Influence in Dissimilar Friction Stir Welding of Aluminium Alloys (AA5083 and AA7068)

Microstructure and corrosion behavior of bobbin tool friction stir welded 2219 aluminum alloy

Parametric effect on microstructure evolution, grain size and mechanical behaviour of friction stir butt welding of AA6061-T6 alloy

Optimization and Characterization Studies of Dissimilar Friction Stir Welding Parameters of Brass and Aluminum Alloy 6063 Using Taguchi

Effect of Tool Pin Profile on Mechanical and Metallurgical Properties of the Friction Stir Welded Joint of AA6061 and AZ91D

Impact of ultrasonic vibration power and tool pin profile on mechanical and microstructural behaviour of friction stir welded dissimilar aluminium alloy joints

Investigation of metallurgical characterization and mechanical properties of double-sided friction stir welding of aluminum 6061 T6 alloy

Optimization of process parameters of friction stir welded joints of dissimilar aluminum alloy by response surface methodology

Comparative Analysis of Microstructure Evolution and Mechanical Properties of Dissimilar Welded Joints of AA7075/AA6061 via Friction Stir Welding, Tungsten Inert Gas Welding, and Tungsten Inert Gas + Friction Stir Processing

Experimental investigation and optimization of mechanical properties on combination of higher and lower strength of aluminum alloys

Thermal Cycling, Microstructure, and Mechanical Properties of Al-Mg-Si-Cu Alloy Bobbin Tool Friction Stir Welded Joints Based on Thermal Index