Amorphous MnCO 3 /C Double Layers Decorated on BiVO 4 Photoelectrodes to Boost Nitrogen Reduction

Dongtian Sun,Hongye Bai,Yong Zhao,QianXiao Zhang,Yajie Bai,Ying Liu,Xuliang Pang,Fagen Wang,Jinrui Ding,Dongbo Xu,Weiqiang Fan,Weidong Shi

DOI: https://doi.org/10.1021/acsami.0c16337

2020-11-10

Abstract:NH₃ is mainly obtained by the Haber–Bosch method in the process of industrial production, which is not only accompanied by huge energy consumption but also environmental pollution. The reduction of N₂ to NH₃ under mild conditions is an important breakthrough to solve the current energy and environmental problems, so the preparation of catalysts that can effectively promote the reduction of N₂ is a crucial step. In this work, BiVO₄ decorated with amorphous MnCO₃/C double layers has been successfully synthesized by a one-step method for the first time. The C and MnCO₃ have been formed as ultrathin film, which enables the establishment of a uniform and tight interface with BiVO₄. The temperature-programmed desorption of N₂ (N₂-TPD) spectra confirmed that the MnCO₃/C could endow BiVO₄ with a drastic enhancement of the chemical absorption ability of a N₂ molecule compared with the pristine BiVO₄. Meanwhile, the method of isotope labeling proved that the catalyst exhibited excellent selectivity for the photocatalytic nitrogen reduction reaction (NRR). The production rate of NH₃ up to 2.426 mmol m^–2 h^–1 has been achieved over the BiVO₄/MnCO₃/C, which is almost 8 times that of pristine BiVO₄. The promoted production rate of NH₃ over BiVO₄/MnCO₃/C could be mainly attributed to the cooperative process between MnCO₃ and C amorphous layers. Therefore, this work could provide an alternative insight to understand the NRR process based on the model of a hierarchical amorphous structure.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c16337?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c16337</a>.Configuration for NRR (Figure S1); the calibration curve used for the calculation of the concentration of NH₄Cl (Figure S2); the XRD patterns of BiVO₄ and BiVO₄/MnCO₃/C (Figure S3); the selective EDS spectra of BiVO₄/MnCO₃/C (Figure S4); the transient photocurrent curves of BiVO₄ and BiVO₄/MnCO₃/C (Figure S5); the FTIR spectra of the standard NH₄Cl solution (Figure S6); the stability of BiVO₄/MnCO₃/C (Figure S7); the fitted results of the PEIS curves in <a class="internalNav" href="#fig3">Figure </a><a class="internalNav" href="#fig3">3</a>b (Table S1); and the comparison of relevant catalysts toward NRR (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c16337/suppl_file/am0c16337_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology