(Bi0.5Na0.5)TiO3-based relaxor ferroelectrics with enhanced energy-storage density and efficiency under low/moderate - fields via average ionic polarizability design

Zepeng Wang,Lixue Zhang,Ruirui Kang,Weijie Yang,Liqiang He,Pu Mao,Xiaojie Lou,Lin Zhang,Jiping Wang

DOI: https://doi.org/10.1016/j.cej.2021.133716

IF: 15.1

2022-03-01

Chemical Engineering Journal

Abstract:Electrostatic capacitors are promising candidates in the application of pulse-power systems due to their high power density and fast charge-discharge rate. However, the insufficient recoverable energy density (W rec) and energy efficiency (η) under low/moderate electric field is still the bottleneck for their applications in miniaturized equipment and portable devices. In this work, we utilize an average ionic polarizability design strategy to enhance W rec by sustaining the high-polarization gene of the system and simultaneously improve η by disrupting the polar order in (1-x)[0.7Bi0.5Na0.5TiO3-0.3Sr0.7Bi0.2TiO3]-xSr(Zn1/3(Nb0.85Ta0.15)2/3)O3 ceramics. As a result, excellent energy-storage properties have been achieved both in low-field (W rec ∼ 2.7 J/cm3 and high η ∼ 93% at 200 kV/cm) and moderate-field (W rec ∼ 5.2 J/cm3 and η ∼ 91% at 330 kV/cm) for x = 0.12 sample. Additionally, the x = 0.12 sample exhibits good thermal stability (−50 ∼ 200 ℃), frequency stability (0.5 ∼ 500 Hz) and cycle stability (105 cycles). Hence, the current work may provide some novel perspectives for improving the W rec and η of dielectric capacitors under low/moderate electric fields.

engineering, chemical, environmental