Organosolv Lignin Improved Thermoplastic Elastomeric Behavior of Polyethylene/Polyisoprene Blend
Arun Ghosh
DOI: https://doi.org/10.1021/acsomega.1c06062
IF: 4.1
2022-03-01
ACS Omega
Abstract:Thermoplastic elastomers are considered the fastest-growing elastomers in recent years because of their thermomechanical recyclability, in contrast to traditional thermoset rubbers. Polyolefins such as low-density polyethylene (LDPE) show low mechanical properties, particularly poor elongation when compared with an elastomer or rubber. In this study, LDPE resin is converted to highly ductile rubber-like materials with high elongation and low modulus properties on blending with polyisoprene rubber (IR), followed by treating with dicumyl peroxide as a curing agent and organosolv lignin as an additive. The technique of high shear melt-mixing, in conjunction with vulcanization or crosslinking using organic peroxide, is used to develop hybrid materials based on the LDPE/IR blend at a 70/30 mass ratio, where LDPE is replaced partly with lignin. Various characteristics such as tensile, viscoelasticity, melt flow, crystallinity, and phase morphology of the materials are analyzed. As expected, vulcanization with peroxide can improve the mechanical performance of the LDPE/IR blends, which is further improved with the application of lignin (2 to 5 wt. %), particularly tensile strain is profoundly increased. For example, the average values of the tensile strength, the modulus, and the ultimate elongation of neat LDPE resin are 7.8 MPa, 177 MPa, and 62%, respectively, and those of LDPE/IR/lignin/DCP 65/30/05/2 are 8.1 MPa, 95 MPa, and 238%, respectively. It indicates that the application of lignin/DCP has a profound effect on improving the ductility and elastomeric characteristics of the materials; thus, this material can have the potential to replace traditional rubber products.This article has not yet been cited by other publications.
chemistry, multidisciplinary