Abstract:Amorphous indium gallium zinc oxide (a-IGZO) thin-film transistors (TFTs) have attracted considerable attention for cutting-edge and next-generation electronics applications because of their high field-effect mobility, low leakage current, superior uniformity, and high transparency. On the other hand, maintaining stable electrical performance under the influences of various ambient effects and complex operating environments is a serious application problem. Hence, a fluoroacrylate-incorporated polytetrafluoroethylene (F–P) is proposed as a new material for passivation layers (PVLs) of a-IGZO TFTs. Solution process-based F–P PVLs were introduced to overcome the intrinsically brittle nature of inorganic materials and enhance the long-term stability of organic materials because of their excellent flexibility, hydrophobic, and chemical stability. This also provides a simple and cheaper alternative for practical applications. The F–P PVLs with different concentrations exhibited appropriate improvements in stability and electrical performance. Of these, the 1.0 wt. % F–P passivated IGZO TFTs showed improved performance in saturation mobility ( μ sat ) from 6.23 ± 0.21 to 7.02 ± 0.38 cm 2 /Vs, an on-off current ratio ( I on / I off ) from (4.05 ± 0.84) × 10 5 to (3.75 ± 2.32) × 10 8 , and a subthreshold swing ( SS ) from 1.79 ± 0.30 to 0.41 ± 0.04 V/decade compared to the pristine device without the F–P PVL. After the 15-day stability test via ambient effects, μsat increased from 7.02 ± 0.38 to ~8 cm 2 /Vs; I on / I off increased from (3.75 ± 2.32) × 10 8 to ~10 10 and the SS values were maintained at a low level (≤ 0.6 V/dec.). The improvement was induced by lower surface energy and better hydrophobicity from F–P PVLs, which can effectively reduce the adsorption behavior of H 2 O and O 2 . With a lower oxygen-related interface trap density, the electrical performances were improved by a suitable concentration-based F–P PVL. In addition, the F–P PVL can provide a long-term guarantee of stability and reliability for a-IGZO TFTs, which will have potential applications for wearable devices and multi-environment electronics devices.

Fluorine passivation of metal surface for self-cleaning semiconductor equipment

Fabrication of Self-Cleaning Polyvinylidene Fluoride Film

Enhanced Surface Passivation of Subnanometer Silicon Dioxide Films by Superacidic Treatments

Passivation mechanisms and pre-oxidation effects on model surfaces of FeCrNi austenitic stainless steel

Fabrication of superhydrophilic or superhydrophobic self-cleaning metal surfaces using picosecond laser pulses and chemical fluorination

Long-Lasting Low Fluorinated Stainless Steel Hierarchical Surfaces for Omniphobic, Anti-Fouling and Anti-Icing applications

Voltage-Controlled Anodic Oxidation of Porous Fluorescent SiC for Effective Surface Passivation

High-Temperature Passivation of the Surface of Candidate Materials for MSR by Adding Oxygen Ions to FLiNaK Salt

A simple strategy towards construction of fluorine-free superhydrophobic aluminum alloy surfaces: self-cleaning, anti-corrosion and anti-frost

Femtosecond laser surface roughening and pulsed plasma polymerization duplex treatment on medical-grade stainless steel substrates for orthodontic purpose

Fabrication of a Fluorocarbon Low Surface Energy Coating for Anti-Stain Applications

Ultrathin Aluminum Oxide Films Induced by Rapid Thermal Annealing for Effective Silicon Surface Passivation

Improving Silicon Surface Passivation with a Silicon Oxide Layer Grown via Ozonated Deionized Water

Aluminum Oxide Deposited by Pulsed-DC Reactive Sputtering for Crystalline Silicon Surface Passivation

Dense Amorphous Passivation Layer Formed on Aluminum Alloy Surfaces by Femtosecond Laser-Assisted Oxygen-Rich Doping

Influence of Fluorine on the Conductivity and Oxidation of Silicon Nanomembranes after Hydrofluoric Acid Treatment

Surface Passivation Properties of ${\textrm{hfo}}_{2}$ Thin Film on N-Type Crystalline Si

Surface Passivation Engineering Approach to Fluoroacrylate-Incorporated Polytetrafluoroethylene for Highly Reliable a-IGZO TFTs

Effects of Fluorine Plasma Treatment on Au-Free Ohmic Contacts to Ultrathin-Barrier AlGaN/GaN Heterostructure

Metallization introduced corrosion and parylene protection of surface micromachined polysilicon film with submicron capacitive gap

Exclusively Gas-Phase Passivation of Native Oxide-Free Silicon(100) and Silicon(111) Surfaces