Complex magnetic interactions and critical behavior analysis in quaternary CoFeV0.8Mn0.2Si Heusler alloy

Dutt Gupt,P. D. Babu,R. S. Dhaka,Guru Dutt Gupt

DOI: https://doi.org/10.1063/5.0196940

IF: 2.877

2024-02-27

Journal of Applied Physics

Abstract:We investigate the magnetic behavior and critical exponents of quaternary CoFeV0.8Mn0.2Si Heusler alloy to understand the interactions across the Curie temperature (TC). The Rietveld refinement of the x-ray diffraction pattern with the space group F4 ̄3m confirms a single-phase cubic Y-type crystal structure. The magnetic susceptibility χ(T) data show a ferromagnetic nature with a second-order phase transition from paramagnetic to ferromagnetic at 446±1 K. The saturation magnetization at 5 K is found to be 2.2 μB/f.u., which is close to the Slater–Pauling rule and indicates its half-metallic nature. The values of asymptotic critical exponents (β, γ, and δ) and the TC are extracted through detailed analytical analysis including the modified Arrott plot, the Kouvel–Fisher (K–F) method, and the Widom scaling relation. Interestingly, the estimated values of β=0.369 and γ=1.445 closely approximate the theoretical values of the 3D Heisenberg model across the TC and validate the second-order thermodynamic phase transition. The obtained exponents lead to the collapse of renormalized isotherms, represented by the relationship between the magnetization (m) and the applied magnetic field (h), into two distinct branches above and below the TC, which validates the reliability of the analysis. Furthermore, these exponents suggest that the spin interaction follows a decay pattern of J(r)∼r−4.99, indicating a short-range magnetic ordering, akin to the itinerant-electron 3D Heisenberg model.

physics, applied

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the complex magnetic interactions and critical behaviors of the quaternary CoFeV\(_{0.8}\)Mn\(_{0.2}\)Si Heusler alloy near the Curie temperature (\(T_C\)). Specifically, through magnetic susceptibility measurement and critical exponent analysis, the author explored the phase transition process from the paramagnetic state to the ferromagnetic state and the nature of magnetic interactions in this process.

### Main research contents:
1. **Confirmation of material structure**: Through X - ray diffraction (XRD) and Rietveld refinement method, it was confirmed that the CoFeV\(_{0.8}\)Mn\(_{0.2}\)Si sample has a single - phase cubic Y - type structure with the space group F/C2243m.
2. **Analysis of magnetic behavior**: The change of the magnetic susceptibility of the sample with temperature was studied, and it was found that a second - order phase transition from the paramagnetic state to the ferromagnetic state occurs near 446 K. The saturation magnetization is 2.2 \(\mu_B/\)f.u. at 5 K, which conforms to the Slater - Pauling rule, indicating its half - metallic characteristics.
3. **Extraction of critical exponents**: Through the modified Arrott plot, Kouvel - Fisher method and Widom scaling relation, the critical exponents \(\beta\), \(\gamma\) and \(\delta\) were extracted. The values of these exponents (\(\beta = 0.369\), \(\gamma = 1.445\)) are close to the theoretical values of the three - dimensional Heisenberg model, verifying the existence of the second - order thermodynamic phase transition.
4. **Analysis of magnetic interactions**: Through the critical exponents, the attenuation mode of the spin interaction was deduced as \(J(r)\sim r^{- 4.99}\), indicating that the magnetic order in the sample is of the short - range three - dimensional Heisenberg type.

### Research significance:
- **Understanding magnetic interactions**: Through detailed critical behavior analysis, the magnetic interaction mechanism of the quaternary CoFeV\(_{0.8}\)Mn\(_{0.2}\)Si Heusler alloy near the Curie temperature was revealed.
- **Verifying theoretical models**: The experimental results are consistent with the theoretical predictions of the three - dimensional Heisenberg model, providing an important experimental basis for understanding and applying such materials.
- **Potential applications**: Due to their unique magnetic and semi - metallic properties, such materials have broad application prospects in spintronics and thermoelectric fields.

### Conclusion:
Through systematic experimental and theoretical analysis, this study successfully analyzed the magnetic interactions and critical behaviors of the CoFeV\(_{0.8}\)Mn\(_{0.2}\)Si Heusler alloy near the Curie temperature, providing an important reference for in - depth understanding of the physical properties of such materials.