Abstract:In recent years, the ablative discharge of the buffer layer in high‐voltage (HV) cross‐linked polyethylene (XLPE) cables has become a significant challenge for the operation and maintenance of power lines. However, there is a lack of effective methods to address buffer layer discharge defects. A practical approach is proposed to repair buffer layer defects and mitigate the associated discharge issues. To achieve this goal, the principles of repairing buffer layer defects are analysed by establishing an electrical network model that considers different contact states between the buffer layer and aluminium sheath. Based on this analysis, a method involving the injection of solidifiable rejuvenation fluid between the buffer layer and aluminium sheath is proposed to effectively suppress buffer layer discharge defects. Through simulation calculations, the minimum electrical conductivity and injection volume required to establish a reliable electrical connection between the buffer layer and aluminium sheath is determined. Additionally, a curable rejuvenation fluid containing conductive carbon black silicone rubber is prepared and analysed for its conductivity and flow properties at both the mesoscopic and macroscopic levels. Finally, a real cable office discharge test is conducted to compare the discharge behaviour of defective cables before and after repair. The results demonstrate that when the conductivity of the rejuvenation fluid exceeds 10−6 S/m, it effectively establishes a conductive channel between the insulation shield and aluminium sheath, thereby reducing the risk of discharge ablation. Furthermore, after injecting the rejuvenation fluid and completely covering the white mark defect, the discharge phenomenon in the buffer layer is significantly suppressed, leading to the restoration of its electrical performance.

Hydrogen evolution and electromigration in the corrosion of aluminium metal sheath inside high‐voltage cables

Feasibility of non-destructive testing for aluminium sheaths of HV cables using ultrasonic guided waves

Corrosion-Fatigue Analysis of Wires in Bridge Cables Considering Time-Dependent Electrochemical Corrosion Process

Breakdown Characteristics and Electrical Life Time Evaluation of 525 Kv EHVDC Cable Insulation at Different Temperatures

AC corrosion analysis of the buffer layer in HV corrugated-aluminum sheathed power cables

Investigation on Dielectric Insulation Properties of ±525 Kv HVDC XLPE Material for High Temperatures Applications

Effect of Tensile Stress on Insulation Properties of 500 Kv EHVAC XLPE Cable under Multi-Field Ageing

Investigation on AC corrosion of aluminum alloy sacrificial anode in the artificial simulated seawater environment

Study on arc duration and erosion characteristics of cable electrodes in AC series circuits

Revitalising high voltage cable: Exploring effective repair methods and influential factors for buffer layer defects using conductive silicone rubber

Aluminum Corrosion Chemistry in High-Voltage Lithium Metal Batteries with LiFSI-Based Ether Electrolytes

Research on the corrosion behavior of underground cables influenced by different ions

On-line Monitoring, Data Analysis for Electrolytic Corrosion of ±800 Kv High Voltage Direct Current Insulators

Flammability degradation behavior and ageing mechanism of flame-retardant cable sheath under different ageing conditions

Experimental study on corrosion resistance of Zn–Al–Mg alloy coating of high-strength steel wires for bridge cables

Highly conductive polymer nanocomposites for emerging high voltage power cable shields: experiment, simulation and applications

Influence and Mechanism Analysis of Acid or Alkali Damp Environment on Insulation Performance of Distribution Cable Accessories

Insulating Properties of Low Density Polyethylene/Alumina Nanocomposites

Experimental Study on the Characterization of Aging Resistance Properties of Optical Cables in the Hydrogen-Containing Downhole Environment

Gas production analysis for the buffer layer of high‐voltage cross‐linked polyethylene cables

Improved Mechanical Property and Corrosion and Wear Resistance of High-Voltage Aluminium Wires by Micro-Arc Oxidation Coating