Abstract:The reduction of platinum use and improvement of its catalytic performance has become the most critical steps to accelerate the development of proton-exchange membrane fuel cells (PEMFCs). Here we report a novel and facile method to boost the performance of the Pt-cased catalyst by integrating with an atomic platinum-group metal (PGM)–free active sites. Using iron-doped zeolitic imidazolate framework-8 (ZIF-8) derived carbon as support, we achieved a uniform deposition of Pt and intermetallic Pt-Co nanoparticles (NPs) through one-step synthesis, with average particle size 2.4 nm for Pt, 3.4 nm for L10 PtCo, and 4.2 nm for L12 Pt3Co. Besides, easy phase transfer during synthesis between ordered intermetallic structures L10 PtCo and L12 Pt3Co was achieved, and a comprehensive comparison between their catalytic performance was established. Synergistic catalysis between Pt or Pt-Co NPs over a PGM–free catalytic substrate derived from iron-doped ZIF-8 led to excellent oxygen reduction reaction (ORR) performance under both rotating disk electrode (RDE) and membrane electrode assembly (MEA) testing. Resulting pure Pt catalysts achieved ORR mass activities of 0.451 A/mgPt and retained 80% initial values after 30,000 voltage cycles in a fuel cell, superior to the DOE 2020 targets without using Pt alloy. Both PtCo and Pt3Co catalysts achieved better performance and exhibited all-sided excellence among mass activity, stability, and power density. Among them, Pt3Co reached the power density at 0.67 V of 923 mW/cm2 and retained 86% initial mass activity after 30,000 voltage cycles in a fuel cell. Their performance dependences on support material particle size and ionomer content were discussed and optimized in MEAs.

Features of behavior and morphological stability of the N-doped PtCu/C catalyst

Deciphering nanostructural evolution of PtCu/C–N electrocatalyst via identical location transmission electron microscopy imaging: Gram-scale synthesis and superior activity in oxygen reduction reaction

Influence of a carbon support on the catalytic activity and durability of the Pt-based electrocatalysts

Electrochemical Activation and Its Prolonged Effect on the Durability of Bimetallic Pt-Based Electrocatalysts for PEMFCs

Tracking the Early-life of PtNi/C Shape-Controlled Catalysts upon their Integration in PEMFC

Tuning the surface structure and phase structure of PtCu 3 nanoparticle for highly efficient electrocatalysts

Optimization of Pt-Ni Alloy Catalysts Synthesized by Potentiostatic Electrodeposition for Cathode in PEMFC

Preparation and Application in Assembling High-Performance Fuel Cell Catalysts of Colloidal PtCu Alloy Nanoclusters

Unveiling the Degradation of Pt/NbOx/C Catalysts in PEMFCs via In Situ X-ray Absorption Spectroscopy

Pt3Co/C Catalyst on the Nitrogen-Doped Carbon Support with High Catalytic Activity and Stability

Characterization of Dealloyed Catalysts in PEMFC

A P–O functional group anchoring Pt–Co electrocatalyst for high-durability PEMFCs

Ultrathin Ni–N–C layer modified Pt–Ni alloy nanoparticle catalysts for enhanced oxygen reduction

The integrated study of the morphology and the electrochemical behavior of Pt-based ORR electrocatalysts during the stress testing

Study on Platinum and Copper Nanosheets Alloys Supported on Mesoporous Titanium Dioxide Doped with Carbon Black As Electrocatalysts in Pem Fuel Cells

Highly dispersed ultrafine PtCo alloy nanoparticles on unique composite carbon supports for proton exchange membrane fuel cells

Pt Monolayer Shell on Nitrided Alloy Core-A Path to Highly Stable Oxygen Reduction Catalyst

Synergistic effect of Pt-Ni dual single-atoms and alloy nanoparticles as a high-efficiency electrocatalyst to minimize Pt utilization at cathode in polymer electrolyte membrane fuel cells

Activity and Stability of Pt/C and Pt-Cu/C Electrocatalysts

Strong Interaction between Titanium Carbonitride Embedded in Mesoporous Carbon Nanofibers and Pt Enables Durable Oxygen Reduction

Synergy of Pt-Free Single Metal Sites for Promoting Pt and Pt<sub>3</sub>co Ordered Intermetallic Catalysts for Fuel Cells: Performance and Durability Improvements