Effect of leachate composition on the long-term performance of a HDPE geomembrane

Fady B. Abdelaal,R. Kerry Rowe,M. Zahirul Islam

DOI: https://doi.org/10.1016/j.geotexmem.2014.06.001

IF: 5.839

2014-08-01

Geotextiles and Geomembranes

Abstract:Aging of the same geomembrane immersed in the same four synthetic municipal solid waste leachates tested by Rowe et al. (2008) for 2.65 years is continued for an additional 6.5 years (i.e., providing data over more than 9 years of aging). The additional data is used to (a) update the initial estimates for antioxidant depletion stage, and (b) investigate the effect of leachate constituents on the timing and magnitude of the changes in the physical properties of the geomembrane. While all the examined leachates had surfactant and trace metals in common, reduced Leachate 1 (full leachate) had salts and volatile fatty acids (VFAs), Leachate 2 was not reduced and had neither salts nor VFAs, reduced Leachate 3 had salts, reduced Leachate 4 had VFAs, and Leachate 5 was similar to Leachate 2 except that it was reduced. Incubation in all leachates gave very similar predictions of the antioxidant depletion stage, however, the salts in Leachates 1 and 3 are shown to have the largest effect on the geomembrane mechanical properties, especially stress-crack resistance, resulting in a shorter time to nominal failure than for leachates without salts. Furthermore, reduced Leachates 1 and 3 showed faster degradation in stress-crack resistance than Leachate 2 which was not reduced and without salts. Arrhenius modeling is used to extrapolate the time to nominal failure (i.e., a reduction in stress-crack resistance to 150 h) at a range of temperatures.

geosciences, multidisciplinary,engineering, geological