On the behavior of nitrogen in a low-Ni high-Mn super duplex stainless steel
Jun Li,Zhenghuan Ma,Xueshan Xiao,Junliang Zhao,Laizhu Jiang
DOI: https://doi.org/10.1016/j.matdes.2010.11.021
IF: 9.417
2011-01-01
Materials & Design
Abstract:The present work describes an investigation on a new series of low-Ni high-Mn super duplex stainless steels (DSSs) 25Cr–2Ni–3Mo–10Mn– x N with nitrogen concentrations varying in the range between 0.37 and 0.50 wt.%. It was observed that these alloys have a ferrite–austenite structure. Under the same heat-treatment conditions, the austenite shows a marked upward tendency with an increase in N content. Nitrogen delays the precipitation of σ phase. The increase in nitrogen enhances the yield strength (YS), ultimate tensile strength (UTS) and ductility as well as the pitting corrosion potential of the materials. The pitting corrosion occurs in the austenite phases in the case of low N content (0.37 wt.%), but in the case of high N content (0.50 wt.%) it happens in the ferrite phases. Keywords A. Ferrous metals and alloys F. Microstructure E. Corrosion 1 Introduction The industrial use of duplex stainless steel (DSS) with a microstructure consisting primarily of ferrite ( α ) and austenite ( γ ) with approximately a 1:1 ratio is rapidly increasing due to the combined advantages of better mechanical and corrosion properties [1–3] . So, an increased application of DSS is found in the energy production, transportation, oil and gas and chemical process industries. In the DSS, nickel acts as an austenite stabilizer, but it is expensive and partial or full replacement with manganese and nitrogen is a cost benefit. Manganese is generally considered to be an austenite former, however, not as effective as nickel, and this problem can be solved by combining Mn with N in these stainless steel alloys. Nitrogen has an austenite-stabilizing effect equivalent to 30 times that of Ni and therefore can replace the expensive Ni, and a big effect of pitting corrosion resistance equivalent to 16 times of Cr, and, in addition, enhances mechanical properties even with a small amount like 0.1–0.3 wt.% [4,5] . Due to their unique advantages, the importance of high nitrogen duplex stainless steels is continuously growing. Previously, the authors developed a family of high manganese and nitrogen super duplex stainless steel 25Cr–2Ni–3Mo– x Mn–N, of which the pitting resistance equivalence (PRE) are greater than 40, and reported the effect of Mn on the microstructure, mechanical and corrosion properties of the alloys by the changes in the volume fraction of austenitic phase [6] . So, in the present work, a series of low-Ni high-Mn super DSSs 25Cr–2Ni–3Mo–10Mn– x N with various nitrogen contents were fabricated, and the effect of nitrogen on the microstructure, the tensile and corrosion behaviors of the alloys were examined. 2 Experimental The duplex stainless steels were designed using the thermodynamic calculation incorporating experimental data and the raw material was melted in a 50 kW induction furnace. MnN master alloy was used for adding nitrogen. The chemical compositions of the castings, designated as N1, N2, N3, and N4 are shown in Table 1 . In this experiment, the casting ingots with a diameter of 120 mm were hot forged into Φ 30 mm sticks, and the as-forged samples were solution-treated at a temperature between 850 and 1300 °C for 30 min and water quenched. The microstructures of the specimens were observed by optical microscopy, and the specimens were electrochemically etched by 10 wt.% KOH solutions, which made the austenite phase bright and the ferrite phase dark. The volume fraction of ferrite was measured with quantitative metallographic analysis systems. The average of 10 measurements on each sample was taken as the volume fraction of ferrite. The transmission electron microscope (TEM) foils were prepared by jet polishing with an 80 vol.% anhydrous alcohol and 20 vol.% perchloric acid (HClO 4 ) solution under liquid nitrogen cooling, applying 45 V. Tensile tests were made at room temperature with specimens having a gage length of 25 mm and diameter of 5 mm according to the National Standard of the P.R.C., GB/T 228-2002, and carried out at a strain rate of 1 × 10 −3 /s. For the study of pitting corrosion behavior, polarization tests of each sample were performed at least three times using an EG&G Princeton Applied Research Potentiostat/Galvanostat Model 273A. Pitting corrosion samples were progressively wet ground down to 800 grit sand paper and then well rinsed in water, and the edges of the exposed sample were masked with an epoxy resin. Then, the samples with an area of 1 cm 2 were tested in 1 mol/L NaCl solution held at 25 °C. Before the scan was initiated, the samples were allowed to remain in the pitting solution for 10 min so as to reach their free corrosion potential. A scan rate of 0.5 mV/s was used, and a saturated calomel electrode (SCE) was used as a reference. The value of potential exceeding 10 −4 A/cm 2 after a sudden increase in electric current was called the pitting corrosion potential. The critical pitting temperature (CPT) of the DSSs was measured according to ASTM G48E. The samples used for tensile and corrosion tests were solution-treated at 1050 °C for 30 min and water quenched. 3 Results and discussion 3.1 Effect of N on the microstructure of the solution-treated samples The optical microstructures of the 25Cr–2Ni–3Mo–10Mn– x N samples containing 0.37, 0.42, 0.46 and 0.50 wt.% N, treated with solution at 950 °C followed by water quenching are presented in Fig. 1 . It can be seen that the microstructure of solution-treated 25Cr–2Ni–3Mo–10Mn– x N DSSs at 950 °C varied significantly with different N contents. Under such conditions, there are many dark precipitates in the ferrite matrix, preferentially located at the interface between ferrite and austenite. With an increase in N content, the number of precipitates decreased at 950 °C, and their volume fractions in the samples N1, N2, N3 and N4 were about 29.5%, 22.7%, 22.5% and 8.2%, respectively. Fig. 2 shows the microstructure of these alloys treated with solution at 1000 °C. The number of dark precipitates decreased to about 5.8, 4.9, 4.6 and 0.8 vol.%, respectively, in samples N1, N2, N3 and N4. From Figs. 1 and 2 , it was found that the precipitates content in samples shows an obvious decline with an increase in N content from 0.37 to 0.50 wt.%. These precipitates were identified as σ phase by X-ray diffraction analysis, as presented in Fig. 3 , and show different precipitation behavior depending on the N content of the specimens. In the case of low N content (0.37 wt.%), the σ -phase precipitates in almost all areas of the ferrite phase that are surrounded by austenite phase, but in the case of high N content (0.50 wt.%), it just precipitates near phase boundaries. Nitrogen reduces the activity of chromium and molybdenum, thus lowering the driving force for σ -phase precipitation [7,8] . So, the result can probably be explained by the fact that nitrogen lowers the partitioning ratio for chromium, nickel, and molybdenum in the ferrite. Despite the alloys tested here have very high content of nitrogen, the nitride was not observed in the range of the test temperature above mentioned. The σ phases were not found by optical microscopy in all specimens treated with solution at 1020 °C for 30 min. As was expected, TEM analysis showed something on such microstructural components that were undetectable with optical analysis. Fig. 4 presents the TEM micrograph of precipitates in N2 treated with solution at 1020 °C for 30 min, while there is no similar precipitate found in N3 and N4 at the same condition. It seems that with an increase in nitrogen, the precipitates content in the alloys becomes less and less, even naught. The precipitates are identified as σ phase and the EDS measurements in the TEM showed that it is rich in Cr, Mn, Fe, and Mo, and the content of them are 34.18, 20.49, 42.07 and 1.57 wt.%, respectively. The result further confirmed that nitrogen delays the precipitation of σ . The optical microstructures of the 25Cr–2Ni–3Mo–10Mn– x N samples with different solution treatment temperatures from 1050 to 1300 °C followed by water quenching are presented in Figs. 5 and 6 . As can be seen in Fig. 5 , the samples treated with solution above 1050 °C do not show the σ phase and show only dual phase structure of ferrite and austenite. The ferrite volume fractions of N1, N2, N3 and N4 treated with solution at 1050 °C are 59%, 52%, 51%, and 48%, respectively. It can be found that the ferrite content decreases with an increase in N. The alloys treated with solution at 1300 °C still show the dual phase structure of ferrite and austenite, and there is about 31 vol.% of the austenite phase even in N1, which contains the lowest N in comparison with others, as shown in Fig. 6 . Fig. 7 plots the relation of nitrogen to the ferrite volume fraction of 25Cr–2Ni–3Mo–10Mn– x N DSSs with different solution treatment temperatures. It is revealed clearly in the graph that ferrite content increases with heat treatment temperature. However, ferrite content tends to decrease with an increase in N content on the same heat treatment, that is to say, more N content results in a higher austenite volume fraction at the same solution treatment temperature. By increasing the temperature from 1050 to 1300 °C, the volume fraction of the austenite phase shows an obvious downward tendency. The ferrite volume fractions vary from 48% to 69% with an increase in the solution treatment temperature regardless of N content. The sample containing 0.50 wt.% N has a microstructure consisting of ferrite and austenite with approximately a 1:1 ratio in a wide temperature range from 1050 to 1250 °C. Therefore, the optimal ferrite volume fraction of 50% can easily be obtained by choosing 25Cr–2Ni–3Mo–10Mn– x N DSSs with 0.50 wt.% N content. To further confirm the results mentioned above, the phase equilibrium in the N4 DSS alloy was calculated using Thermo-Calc, as shown in Fig. 8 . The model considered the effects of Cr, Ni, Mn, Mo, Fe, C, and N on the presence of ferrite, austenite, σ , nitrides/carbides, and the liquid phases. The calculations indicate that carbides (M 23 C 6 ) and nitrides (HCP) precipitate in the alloy aged between 830 and 920 °C, which also explain why the nitride was not observed in the samples treated with solution between 950 and 1000 °C. The ferrite (BCC) changes to a combination of austenite (FCC) and σ during heating up to 950 °C. Then, ferrite begins to re-form, and σ continues to reduce until it completely disappears at a temperature of approximately 1020 °C. With an increase in temperature, ferrite increases and austenite decreases until they have equal amounts at about 1130 °C. The theoretical calculation of σ precipitates and duplex phase proportion is basically in accordance with the experimental results. 3.2 Effect of N on the mechanical and corrosion property Fig. 9 presents the relation of nitrogen content to the ultimate tensile strength (UTS), yield strength (YS) and elongation of the 25Cr–2Ni–3Mo–10Mn– x N DSSs treated with solution at 1050 °C for 30 min and water quenched. The YS and UTS of N1, N2, N3 and N4 are increasing from 663 to 690 MPa and from 842 to 924 MPa respectively with an increase in nitrogen content. However, it is interesting to note that the tensile elongation also enhanced from 36.7% to 43.4% with this increase in nitrogen. Alloy N1 exhibited the lowest tensile strength, while alloy N4 showed the highest tensile strength and the best elongation. In other words, an increase in austenite volume fraction (or a decrease of ferrite phase) increases the YS, UTS and elongation of the DSSs. Simmons [9] reported that the YS and UTS of austenitic stainless steels increase with N content due to solid-solution-strengthening and nitrogen-enhanced grain size strengthening effects. As all know, most of the nitrogen in DSS is dissolved in austenite, which makes austenite become the stronger phase due to interstitial solid solution strengthening. Generally speaking, the higher strength an alloy has, the lower elongation it tends to have. According to the result obtained above, the austenite content increases with an increase in N content. The austenite phase has more slip planes, which leads to better steel ductility. In this work, the nitrogen content reached 0.50 wt.%, which may explain the results of the tensile tests and the increase in austenite phase as a function of the increase in N. This increase in N enhances the mechanical strength and ductility, due to the interstitial solid solution strengthening and grain boundary strengthening effect of N, and also the change of the ferrite to austenite phase. In order to study the effect of N additions on the pitting corrosion behavior of 25Cr–2Ni–3Mo–10Mn– x N DSSs, polarization tests were conducted at a scanning rate of 0.5 mV/s in 1 mol/L NaCl aqueous solution, at 25 °C. Fig. 10 shows the representative polarization curves for alloys with different N contents. The pitting corrosion potential increased from 1040 to 1170 mV versus SCE with an increase in N content from 0.37 to 0.50 wt.%. Pitting holes of the samples after polarization tests are presented in Fig. 11 . To observe the fact that in which phase the pitting holes are distributed, the specimens were electrochemically etched by 10 wt.% KOH solution and the optical micrographs of pitting hole of them are shown in Fig. 12 . In the case of low N content (0.37 wt.%), the pitting corrosion mainly occurs in the austenite phases, but in the case of high N content (0.50 wt.%), it primarily takes place in the ferrite phases. The pitting corrosion resistance of the alloys is enhanced with an increase in nitrogen. Many researches have concluded that duplex stainless steels obtain high pitting corrosion resistance due to the dual phase structures, containing high nitrogen and some molybdenum. There are also several mechanisms to be suggested to explain how nitrogen operates [10–13] . As discussed above, nitrogen reduces the activity of chromium and molybdenum, which means that the activity of chromium and molybdenum enhance with a decrease in nitrogen content. When the amount of N is 0.37 wt.%, the partitioning ratio of chromium and molybdenum is much bigger in ferrite than in austenite, which leads to better pitting corrosion resistance of ferrite, and the pitting hole occurs in austenite. When the amount of N is 0.50 wt.%, the partitioning ratio of chromium and molybdenum tends to be equivalent in ferrite and austenite. And with the effect of nitrogen, the austenite has a stronger pitting corrosion resistance than ferrite. Therefore, pitting hole takes place in ferrite. The pitting corrosion resistance is often correlated with the chemical composition of stainless steels [14] . It has been suggested that pitting corrosion depends basically on Cr, Mo and N content. The pitting corrosion resistance can be characterized in terms of the pitting resistance equivalence (PRE), which is often defined as [15] : (1) PRE = % Cr + 3.3 % Mo + 16 % N It is well-known that in duplex stainless steel, Cr and Mo enrich in ferrite, whereas Ni and N are concentrated in austenite. So, the pitting corrosion resistance is different between ferrite and austenite. According to formula (1), the PRE values of the ferrite and austenite of the experimental alloys are assessed by phase equilibria computing program Thermo-Calc. The PRE values of the austenite in N1, N2, N3 and N4 are 33.69, 39.06, 43.93 and 46.50 respectively, while that of the ferrite are 40.12, 39.50, 39.41 and 39.43. It can be seen that PRE values of austenite are higher than that of ferrite in N3 and N4, but lower in N1 and N2, which is basically in accordance with the results of the polarization test. The critical pitting temperature (CPT) is the lowest temperature at which the growth of stable pits is possible, and the experimental CPT of the DSSs was measured according to ASTM G48E in 6 wt.% acidified FeCl 3 solution. The solution temperature was increased by 2.5 °C/24 h from 53 to 63 °C. The CPT results for alloys N1, N2, N3 and N4 are shown in Table 2 . The pitting corrosion occurred at 60.5–63 °C, and the CPT presents an increase tendency with nitrogen content. The CPT may be estimated by the following equation [16,17] : (2) CPT ( ° C ) = 2.5 × % Cr + 7.6 × % Mo + 31.9 × % N - 41.0 The CPT values of N1, N2, N3 and N4 calculated with formula (2) are 56.6 °C, 58.5 °C, 61.2 °C and 61.1 °C respectively. The theoretical values of CPT are approximately consistent with the experimental ones. 4 Conclusions The microstructure, tensile and corrosion behaviors of a new low-Ni high-Mn 25Cr–2Ni–3Mo–10Mn– x N DSSs with different N contents of 0.37, 0.42, 0.46 and 0.50 wt.%, respectively, were examined. The designed alloys have a ferrite–austenite structure in a wide range of experimental heat treatment temperature. The ferrite content in 25Cr–2Ni–3Mo–10Mn– x N DSSs tends to decrease with an increase in N content. Regardless of N content, the ferrite volume fractions vary from 48% to 69%, with an increase in the temperature from 1050 to 1300 °C. With an increase in N content, mechanical strength and elongation of the alloys both increased, which is due to the interstitial solid solution strengthening and grain boundary strengthening effect of N, and also the change of the ferrite to austenite phase. The pitting corrosion potential of the DSSs rises with an increase in N content from 0.37 to 0.50 wt.%. The pitting corrosion mainly occurs in the austenite phases in the case of low N content (0.37 wt.%), but in the case of high N content (0.50 wt.%) it happens in the ferrite phases. Nitrogen increases the corrosion resistance of austenite. Acknowledgement All the authors are grateful to the support provided by the key project of Science and Technology Commission of Shanghai Municipality under Contract No. 065211026. References [1] R. Kaçar Effect of solidification mode and morphology of microstructure on the hydrogen content of duplex stainless steel weld metal Mater Des 25 2004 1 9 [2] B. Deng Y. Jiang J. Gong Critical pitting and repassivation temperatures for duplex stainless steel in chloride solutions Electrochim Acta 53 16 2008 5220 5225 [3] H. Farnoush A. Momeni K. Dehghani Hot deformation characteristics of 2205 duplex stainless steel based on the behavior of constituent phases Mater Des 31 2010 220 226 [4] Kearns JR. The effect of nitrogen on the corrosion resistance of austenitic stainless alloys containing molybdenum. In: Lula RA, editor. New Developments in stainless steel technology. Metals Park, OH: ASM; 1985. p. 117–27. [5] C.E. Bates O.V. Rogers R.W. Monroe Effects of nitrogen additions on CF-3 and CF-8 stainless steel R.A. Lula New developments in stainless steel technology 1985 ASM Metals Park, OH 207 220 [6] J. Li Y. Xu X. Xiao A new resource-saving, high manganese and nitrogen super duplex stainless steel 25Cr–2Ni–3Mo– x Mn–N Mater Sci Eng A 527 1–2 2009 245 251 [7] L. Weber P.J. Uggowitzer Partitioning of chromium and molybdenum in super duplex stainless steels with respect to nitrogen and nickel content Mater Sci Eng A 242 1–2 1998 222 229 [8] M. Cortie J. Potgieter The effect of temperature and nitrogen content on the partitioning of alloy elements in duplex stainless steels Metall Mater Trans A 22 10 1991 2173 2179 [9] J.W. Simmons Overview: High-nitrogen alloying of stainless steels Mater Sci Eng A 207 2 1996 159 169 [10] G.C. Palit V. Kain H.S. Gadiyar Electrochemical investigations of pitting corrosion in nitrogen-bearing type 316N stainless steel Corrosion 49 12 1993 979 991 [11] Y.C. Lu R. Bandy C.R. Clayton Surface enrichment of nitrogen during passivation of a highly resistant stainless steel J Electrochem Soc 130 1983 1774 1776 [12] H.P. Leckie H.H. Uhlig Environmental factors affecting the critical potential for pitting in 18–8 stainless steel J Electrochem Soc 113 12 1966 1262 1267 [13] R.C. Newman T. Shahrabi The effect of alloyed nitrogen or dissolved nitrate ions on the anodic behaviour of austenitic stainless steel in hydrochloric acid Corros Sci 27 8 1987 827 838 [14] R. Merello F.J. Botana J. Botella Influence of chemical composition on the pitting corrosion resistance of non-standard low-Ni high-Mn–N duplex stainless steels Corros Sci 45 2003 909 921 [15] G. Herbsleb Influence of SO 2 , H 2 S and CO on pitting corrosion of austenitic chromium–nickel stainless steels with up to 4 wt.% molybdenum in 1 M NaCl Werkstoffe und Korrosion 33 6 1982 334 340 [16] R.J. Brigham E.W. Tozer Effect of alloying on pitting resistance of 18% Cr austenitic stainless steels Corrosion 30 5 1974 161 166 [17] M. Renner U. Heuber M.B. Rockel Temperature as a pitting and crevice corrosion criterion in the ferric chloride test Werkstoffe und Korrosion 37 1986 183 190